Abstract: Described herein is a multi-phase polymer binder including an aqueous polymer dispersion, an optional hydrophobic emulsion, and an optional surfactant. The polymer binder, when dried, provides a water uptake of less than about 5 g/m2/20 min, a seal strength of at least about 200 Newton/meter (N/m) as measured at 25° C. or at 90° C., and sufficient block resistance to impart no substrate damage.

Abstract: Disclosed herein is a composition that can provide moisture barrier during packaging. Additionally disclosed herein is a substrate coated with the composition that is recyclable and repulpable. The composition includes at least one ester and at least one styrene acrylic copolymer with a glass transition temperature in the range of from -54° C. to 10° C.

Abstract: A process of preparing an aqueous solution of a cycloimide-containing polymer includes heating an aqueous solution of a cycloanhydride-containing polymer with a first neutralizing agent at a ratio of cycloanhydride to neutralizing agent of about 1:1 to about 1:1.5 at a temperature and for a time sufficient to form the aqueous solution of the cycloimide-containing polymer having a cycloimide to acid group ratio of about 1:2 to about 1.5:2.

Abstract: Disclosed herein include methods of reducing the viscosity of a starch slurry during starch processing by the addition of one or more surfactants and one or more amylases. In some embodiments, the unexpected reduction in slurry viscosity results in a surprising increase in corn oil recovery, reduction in residual starch, and increased fermentation rate.

Abstract: Disclosed herein include methods of reducing the viscosity of a starch slurry during starch processing by the addition of one or more surfactants and one or more amylases. In some embodiments, the unexpected reduction in slurry viscosity results in a surprising increase in corn oil recovery, reduction in residual starch, and increased fermentation rate.

Abstract: Described herein is a multi-phase polymer binder including an aqueous polymer dispersion, an optional hydrophobic emulsion, and an optional surfactant. The polymer binder, when dried, provides a water uptake of less than about 5 g/m2/20 min, a seal strength of at least about 200 Newton/meter (N/m) as measured at 25° C. or at 90° C., and sufficient block resistance to impart no substrate damage.

Abstract: Described herein is a multi-phase polymer binder including an aqueous polymer dispersion, an optional hydrophobic emulsion, and an optional surfactant. The polymer binder, when dried, provides a water uptake of less than about 5 g/m2/20 min, a seal strength of at least about 200 Newton/meter (N/m) as measured at 25° C. or at 90° C., and sufficient block resistance to impart no substrate damage.

Abstract: A process of preparing an aqueous solution of a cycloimide-containing polymer includes heating an aqueous solution of a cycloanhydride-containing polymer with a first neutralizing agent at a ratio of cycloanhydride to neutralizing agent of about 1:1 to about 1:1.5 at a temperature and for a time sufficient to form the aqueous solution of the cycloimide-containing polymer having a cycloimide to acid group ratio of about 1:2 to about 1.5:2.

Abstract: Described herein is a multi-phase polymer binder including an aqueous polymer dispersion, an optional hydrophobic emulsion, and an optional surfactant. The polymer binder, when dried, provides a water uptake of less than about 5 g/m2/20 min, a seal strength of at least about 200 Newton/meter (N/m) as measured at 25° C. or at 90° C., and sufficient block resistance to impart no substrate damage.

Abstract: A process of preparing an aqueous solution of a cycloimide-containing polymer includes heating an aqueous solution of a cycloanhydride-containing polymer with a first neutralizing agent at a ratio of cycloanhydride to neutralizing agent of about 1:1 to about 1:1.5 at a temperature and for a time sufficient to form the aqueous solution of the cycloimide-containing polymer having a cycloimide to acid group ratio of about 1:2 to about 1.5:2.

Abstract: A process of preparing an aqueous solution of a cycloimide-containing polymer includes heating an aqueous solution of a cycloanhydride-containing polymer with a first neutralizing agent at a ratio of cycloanhydride to neutralizing agent of about 1:1 to about 1:1.5 at a temperature and for a time sufficient to form the aqueous solution of the cycloimide-containing polymer having a cycloimide to acid group ratio of about 1:2 to about 1.5:2.

Abstract: An aqueous binder composition comprising: a) a water-insoluble polymer (P) in the form of dispersed polymer particles having a glass transition temperature in the range from ?50° C. to 50° C., obtained by free-radical polymerization of ethylenically unsaturated monomers M, the monomers M comprising: 80% to 99.9% by weight, based on the total amount of monomers M, of at least one neutral, monoethylenically unsaturated monomer M1 of low water-solubility; and 0.1% to 20% by weight, based on the total amount of monomers M, of at least one monoethylenically unsaturated monomer M2 which carries at least one carboxyl group and/or at least one carboxamido group (CONH2); and b) boric acid and/or at least one salt of boric acid is provided. Also provided are a process to prepare the binder composition and the use thereof.

Abstract: The present invention relates to binder compositions which are based on polymer dispersions and comprise boric acid or salts of boric acid as crosslinking agents, to processes for preparing them, and to their uses. The aqueous binder composition comprises: a) a water-insoluble polymer (P) in the form of dispersed polymer particles having a glass transition temperature in the range from ?50° C. to 50° C., obtainable by free-radical polymerization of ethylenically unsaturated monomers M, the monomers M comprising: 80% to 99.9% by weight, based on the total amount of monomers M, of at least one neutral, monoethylenically unsaturated monomer M1 of low water-solubility; and 0.1% to 20% by weight, based on the total amount of monomers M, of at least one monoethylenically unsaturated monomer M2 which carries at least one carboxyl group and/or at least one carboxamido group (CONH2); and b) boric acid and/or at least one salt of boric acid.