Abstract: A composition includes polymer and dispersed infrared-reflective clusters of titanium dioxide primary particles. The titanium dioxide primary particles are cemented together with precipitated silica and/or alumina to form clusters. The titanium dioxide primary particles have an average particle diameter in the range of from about 0.15 to about 0.35 micron, while the clusters of titanium dioxide primary particles have an average cluster diameter in the range of from about 0.38 to about 5 microns and a geometric standard deviation (GSD) in the range of from about 1.55 to about 2.5.

Abstract: A composition includes polymer and dispersed infrared-reflective clusters of titanium dioxide primary particles. The titanium dioxide primary particles are cemented together with precipitated silica and/or alumina to form clusters. The titanium dioxide primary particles have an average particle diameter in the range of from about 0.15 to about 0.35 micron, while the clusters of titanium dioxide primary particles have an average cluster diameter in the range of from about 0.38 to about 5 microns and a geometric standard deviation (GSD) in the range of from about 1.55 to about 2.5.

Abstract: A composition includes polymer and dispersed infrared-reflective clusters of titanium dioxide primary particles. The titanium dioxide primary particles are cemented together with precipitated silica and/or alumina to form clusters. The titanium dioxide primary particles have an average particle diameter in the range of from about 0.15 to about 0.35 micron, while the clusters of titanium dioxide primary particles have an average cluster diameter in the range of from about 0.38 to about 5 microns and a geometric standard deviation (GSD) in the range of from about 1.55 to about 2.5.

Abstract: A composition includes polymer and dispersed infrared-reflective clusters of titanium dioxide primary particles. The titanium dioxide primary particles are cemented together with precipitated silica and/or alumina to form clusters. The titanium dioxide primary particles have an average particle diameter in the range of from about 0.15 to about 0.35 micron, while the clusters of titanium dioxide primary particles have an average cluster diameter in the range of from about 0.38 to about 5 microns and a geometric standard deviation (GSD) in the range of from about 1.55 to about 2.5.

Abstract: In various embodiments, methods and compositions are provided comprising titanium dioxide and silica spacers having improved light stability for use in paper, plastic and paints.

Abstract: In various embodiments, methods and compositions are provided comprising titanium dioxide and silica spacers having improved light stability for use in paper, plastic and paints.

Abstract: In various embodiments, methods and compositions are provided comprising titanium dioxide and silica spacers having improved light stability for use in paper, plastic and paints.

Abstract: In various embodiments, methods and compositions are provided comprising titanium dioxide and silica spacers having improved light stability for use in paper, plastic and paints.

Abstract: The present invention provides methods and compositions comprising inorganic solids for use as pigments in paints, papers and plastics.

Abstract: The present invention provides methods and compositions comprising inorganic solids for use as pigments in paints, papers and plastics.

Abstract: A titanium dioxide compound was isolated from a rare type of naturally occurring ore. Processes for efficiently isolating and obtaining these TiO2 compounds, as well as methods for using them have been developed. These TiO2 compounds may be used directly in applications such as paper, plastics and paints without being subjected to the chloride or sulfate processes. Also they made be used as a feedstock for the chloride or sulfate processes. In order to obtain these TiO2 compounds, one may grind or pulverize the naturally occurring ore, disperse it in a solution or suspension, and process it by selective flocculation or aqueous biphasic extraction.

Abstract: The present invention provides slurries and methods of making slurries having improved stability comprising below about 78 weight-percent rutile titanium dioxide based on the total weight of the slurry, an amorphous alumina compound surface treated titanium dioxide, a polyacrylic acid dispersing agent having a molecular weight in the range of from about 2,000 to about 5,000 that is neutralized with a neutralizing agent having a monovalent group, and water; wherein the slurry has a pH of from about 6 to about 8. The slurries of the present invention resist gel formation.

Abstract: The present invention discloses high solids slurries of anatase titanium dioxide pigment comprising greater than about 75% by weight of anatase TiO2 pigment dispersed in water. A process for producing the slurries of the present invention is disclosed which comprises the steps of a) dry milling the anatase titanium dioxide pigment, preferably by pressure rolling, and b) mixing the dry milled pigment with water in the presence of an acrylic acid dispersant.

Abstract: The present invention provides methods and compositions comprising inorganic solids for use as pigments in paints, papers and plastics.

Abstract: A titanium dioxide compound was isolated from a rare type of naturally occurring ore. Processes for efficiently isolating and obtaining these TiO2 compounds, as well as methods for using them have been developed. These TiO2 compounds may be used directly in applications such as paper, plastics and paints without being subjected to the chloride or sulfate processes. Also they made be used as a feedstock for the chloride or sulfate processes. In order to obtain these TiO2 compounds, one may grind or pulverize the naturally occurring ore, disperse it in a solution or suspension, and process it by selective flocculation or aqueous biphasic extraction.

Abstract: The present invention discloses high solids slurries of anatase titanium dioxide pigment comprising greater than about 75% by weight of anatase TiO2 pigment dispersed in water. A process for producing the slurries of the present invention is disclosed which comprises the steps of a) dry milling the anatase titanium dioxide pigment, preferably by pressure rolling, and b) mixing the dry milled pigment with water in the presence of an acrylic acid dispersant.

Abstract: The present invention discloses high solids slurries of anatase titanium dioxide pigment comprising greater than about 75% by weight of anatase TiO2 pigment dispersed in water. A process for producing the slurries of the present invention is disclosed which comprises the steps of a) dry milling the anatase titanium dioxide pigment, preferably by pressure rolling, and b) mixing the dry milled pigment with water in the presence of an acrylic acid dispersant.

Abstract: The present invention discloses high solids slurries of sulfate process, anatase titanium dioxide pigment. The improvements of these slurries over those of the prior art are improved slurry stability, tolerance to calcium and magnesium ions, foaming tendencies and reduced tendency to flocculate. The slurries of the present invention are comprised of at least 65% by weight of anatase TiO.sub.