Abstract: A nickel alloy having superior surface properties by controlling the composition of non-metallic inclusions that affect surface properties, and a method for producing the same. A nickel alloy includes: all by mass %, Ni: 99.0% or more, C: 0.020% or less, Si: 0.01 to 0.3%, Mn: 0.3% or less, S: 0.010% or less, Cu: 0.2% or less, Al: 0.001 to 0.1%, Fe: 0.4% or less, O: 0.0001 to 0.0050% or less, Mg: 0.001 to 0.030%, Ca: 0.0001 to 0.0050%, B: 0.0001 to 0.01%, and the balance of inevitable impurities; the alloy including non-metallic inclusions, in which the non-metallic inclusions include one or more of MgO, CaO, CaO—Al2O3-based oxides, CaO—SiO2-based oxides, CaO—MgO-based oxides, and MgO·Al2O3, the MgO·Al2O3 has a number ratio of number 50% or less with respect to all oxide-based, non-metallic inclusions.

Abstract: Alloy compositions, structures, and production methods for an appropriate slit cut surface shape improve productivity by increasing welding speed and stabilizing quality during high speed welding in Ti-containing Fe—Ni—Cr alloy production. The Ti-containing Fe—Ni—Cr alloy contains, hereinafter in weight %, C: 0.001 to 0.03%, Si: 0.05 to 1.25%, Mn: 0.10 to 2.00%, P: 0.001 to 0.030%, S: 0.0001 to 0.0030%, Ni: 15 to 50%, Cr: 17 to 25%, Al: 0.10 to 0.80%, Ti: 0.10 to 1.5%, N: 0.003 to 0.025%, 0: 0.0002 to 0.007%, Fe as a remainder, and inevitable impurities, and when the number and size of titanium nitrides contained in material are evaluated in a freely selected field of view of 5 mm2, the titanium nitrides having sizes of not more than 15 ?m are not less than 99.3% of total of the titanium nitrides.

Abstract: Fe—Cr—Ni—Mo alloy having superior surface properties and a method for producing the same using a commonly used apparatus at low cost. The Fe—Cr—Ni—Mo alloy has (% indicates mass %): C: ?0.03%, Si: 0.15 to 0.5%, Mn: 0.1 to 1%, P: ?0.03%, S: ?0.002%, Ni: 20 to 32%, Cr: 20 to 26%, Mo: 0.5 to 2.5%, Al: 0.1 to 0.5%, Ti: 0.1 to 0.5%, Mg: 0.0002 to 0.01%, Ca: 0.0002 to 0.01%, N: ?0.02%, O: 0.0001 to 0.01%, freely contained components of Co: 0.05 to 2% and Cu: 0.01 to 0.5%, Fe as a remainder, and inevitable impurities, wherein MgO, MgO.Al2O3 spinel type, and CaO—Al2O3—MgO type are contained as oxide type non-metallic inclusions, ratio of number of MgO.Al2O3 spinel type to all oxide type non-metallic inclusions is ?50%, and CaO—Al2O3—MgO type contains CaO: 30 to 70%, Al2O3: 5 to 60%, MgO: 1 to 30%, SiO2: ?8%, and TiO2: ?10%.

Abstract: Fe—Cr—Ni—Mo alloy having superior surface properties and a method for producing the same using a commonly used apparatus at low cost. The Fe—Cr—Ni—Mo alloy has (% indicates mass %): C: ?0.03%, Si: 0.15 to 0.5%, Mn: 0.1 to 1%, P: ?0.03%, S: ?0.002%, Ni: 20 to 32%, Cr: 20 to 26%, Mo: 0.5 to 2.5%, Al: 0.1 to 0.5%, Ti: 0.1 to 0.5%, Mg: 0.0002 to 0.01%, Ca: 0.0002 to 0.01%, N: ?0.02%, O: 0.0001 to 0.01%, freely contained components of Co: 0.05 to 2% and Cu: 0.01 to 0.5%, Fe as a remainder, and inevitable impurities, wherein MgO, MgO.Al2O3 spinel type, and CaO—Al2O3—MgO type are contained as oxide type non-metallic inclusions, ratio of number of MgO.Al2O3 spinel type to all oxide type non-metallic inclusions is ?50%, and CaO—Al2O3—MgO type contains CaO: 30 to 70%, Al2O3: 5 to 60%, MgO: 1 to 30%, SiO2: ?8%, and TiO2: ?10%.