Abstract: A catalyst carrier comprising gamma alumina wherein the apparent bulk density is in the range of from 0.65 g/cc to 0.71 g/cc, the total pore volume is in the range of from 0.55 cc/g to 0.65 cc/g, the content of pores having a diameter in the range of from 60A to 110A occupies at least 75% of the total pore volume, the surface area is in the range of from 210 m.sup.2 /g to 250 m.sup.2 /g and the attrition loss is less than 0.5 wt. %. This sort of catalyst carrier can be namufactured through a series of steps of: (a) preparing a first alumina hydrosol having an aluminum concentration in the range of from 9.8 wt. % to 14.4 wt. % and a weight ratio of aluminum to chloride in the range of from 0.95 to 1.20, (b) preparing a second alumina hydrosol having an aluminum concentration in the range of from 9.5 wt. % to 13.0 wt. % and a weight ratio of aluminum to chloride in the range of from 0.85 to 0.