Abstract: A squeezable tubular container (a) which is formed from a composition containing a polyethylene having a density of 0.900 to 0.975 g/cm.sup.3 and an ethylene/.alpha.-olefin copolymer having a density smaller than 0.900 g/cm.sup.3, (b) has a crosslinking caused under irradiation with electron beam, and (c) is sterilizable at a high temperature or is heat-sealable or ultrasonically sealable; and a process for the production thereof.

Abstract: A squeezable tubular container (a) which is formed from a composition containing a polyethylene having a density of 0.900 to 0.975 g/cm.sup.3 and an ethylene/.alpha.-olefin copolymer having a density smaller than 0.900 g/cm.sup.3, (b) has a crosslinking caused under irradiation with electron beam, and (c) is sterilizable at a high temperature or is heat-sealable or ultrasonically sealable; and a process for the production thereof.

Abstract: A process for producing a modified polypropylene having a very high melt tension and superior stiffness and moldability, and a molded product obtained by using the modified polypropylene are provided.which process includes adding 0.05 to 10 millimols of a cross-linking auxiliary to 100 g of a linear polypropylene, mixing them, irradiating ionizing radiations to the mixture so as to give an absorbed dosage of 1 to 20 kGy, and successively heat-treating the resulting material at 80.degree. to 350.degree. C.,which modified polypropylene has(A) a degree of branching of substantially 1,(B) a relationship between its melt tension (MS) at 230.degree. C. and its intrinsic viscosity (.eta.) measured in tetralin at 230.degree. C. expressed by an inequalitylog (MS)>4.24.times.log [.eta.]-0.915, and(C) a percentage of extraction residue in boiling xylene of 1% by weight or less.

Abstract: A process for forming a container of acrylonitrile polymers by biaxial-orientation blow-molding a preform. A preform of thermoplastic resin, mainly acrylonitrile polymers, is irradiated with an electron beam or a gamma-ray. Immediately after the irradiation, the preform is heated at 40.degree. C. or higher to reduce residual acrylonitrile monomer in the preform to 0.1 ppm or less. Then, the preform is biaxial-orientation blow molded to form a container.

Abstract: A process for producing a slow-release powder which permit various active ingredients such as perfumes, insect control agents, rust inhibitors, mold inhibitors and antibacterial agents to be slowly released over a prolonged time, the process comprising the steps of mixing a long-chain compound with the ingredients, mixing the resulting mixture with urea, and exposing the resulting urea adduct to radiation.

Abstract: This invention provides a process for preparing a transparent polymeric product free from strain and bubbles and having improved physical and chemical properties. The product can be produced from a bis-allylcarbonate-based monomer mixture by cast polymerization for extremely shortened polymerization time.

Abstract: This invention provides a process for producing a transparent shaped polymeric product which is free from defects such as strain and bubbles and has improved chemical and physical properties. The product is produced from a methyl methacrylate- or methyl acrylate-based monomer mixture by cast polymerization for a significantly shortened time.