Abstract: An aluminium alloy foil with a thickness of maximum 12 ?m, maximum 9 ?m or less than 8 ?m. The aluminium alloy foil is an AA1xxx or A8xxx aluminium alloy in the annealed state. In addition, a method for manufacturing an aluminium alloy foil and its use. The object of proposing an aluminium alloy foil with improved barrier properties, a method for its manufacture and a use of the aluminium alloy foil is achieved in that the aluminium alloy foil has a maximum number of pores with a pore size of 1 ?m to 200 ?m of maximum 12 per dm2, maximum 8 per dm2 or maximum 6 per dm2. In addition, a method is specified for how this aluminium alloy foil can be manufactured.

Abstract: The invention relates to a battery electrode foil comprising an aluminium alloy, wherein the aluminium alloy has the following composition in weight percent: Si: 0.07-0.12% by weight, Fe: 0.18-0.24% by weight, Cu: 0.03-0.08% by weight, Mn: 0.015-0.025% by weight, Zn: ?0.01% by weight, Ti: 0.015-0.025% by weight, Zn: ?0.01% by weight, Ti: 0.015-0.025% by weight, Mn: 0.015-0.025% by weight, Zn: ?0.01% by weight, Ti: 0.015-0.025% by weight, wherein the aluminium alloy can contain impurities up to a maximum of 0.01% in each case, up to a maximum of 0.03% in total, but the proportion of aluminium must be at least 99.5% by weight; wherein the battery electrode foil has intermetallic phases of a diameter length of 0.1 to 1.0 ?m with a density of ?9500 particles/mm2. The invention further relates to a process for the production of a battery electrode foil, its use for the production of accumulators, and accumulators containing the battery electrode foil.

Abstract: The invention relates to a battery electrode foil comprising an aluminium alloy, wherein the aluminium alloy has the following composition in % by weight: Si: 0.01-0.15% by weight, Fe: 0.02-0.4% by weight, Cu: ?0.08% by weight, Mn: ?0.03% by weight, Mg: ?0.03% by weight, Cr: ?0.01% by weight, Ti: 0.005-0, 03% by weight, wherein the aluminium alloy can contain impurities up to a maximum of 0.05% in each case, in total up to a maximum of 0.15%, the remaining % by weight being aluminium, the proportion of aluminium however being at least 99.35% by weight; wherein the battery electrode foil has intermetallic phases with a diameter length of 0.1 to 1.0 ?m with a density of?9500 particles/mm2. The invention further relates to a method for the production of a battery electrode foil, its use for the production of accumulators, and accumulators containing the battery electrode foil.

Abstract: The invention relates to a battery electrode foil comprising an aluminium alloy, wherein the aluminium alloy has the following composition in weight percent: Si: 0.07-0.12% by weight, Fe: 0.18-0.24% by weight, Cu: 0.03-0.08% by weight, Mn: 0.015-0.025% by weight, Zn: ?0.01% by weight, Ti: 0.015-0.025% by weight, Zn: ?0.01% by weight, Ti: 0.015-0.025% by weight, Mn: 0.015-0.025% by weight, Zn: ?0.01% by weight, Ti: 0.015-0.025% by weight, wherein the aluminium alloy can contain impurities up to a maximum of 0.01% in each case, up to a maximum of 0.03% in total, but the proportion of aluminium must be at least 99.5% by weight; wherein the battery electrode foil has intermetallic phases of a diameter length of 0.1 to 1.0 ?m with a density of ?9500 particles/mm2. The invention further relates to a process for the production of a battery electrode foil, its use for the production of accumulators, and accumulators containing the battery electrode foil.