Abstract: This invention relates to a process for making phenolic fatty acid compounds having a reduced phenolic ester content. The invention also relates to method for chemically bonding a phenolic resin with a non-phenolic polymer (e.g., a synthetic fabric). The method comprises contacting a phenolic fatty acid compound with a non-phenolic polymer to introduce a hydroxy phenyl functional group into the non-phenolic polymer; and reacting the hydroxy phenyl functional group contained in the non-phenolic polymer with a phenolic resin or a phenolic crosslinker composition capable of forming a phenolic resin, to chemically bond the phenolic resin with the non-phenolic polymer. The invention is particularly useful for making a synthetic fabric-reinforced article, such as synthetic fabric-reinforced rubber article, circuit board substrate, or fiberglass.

Abstract: This invention relates to a process for making phenolic fatty acid compounds having a reduced phenolic ester content. The invention also relates to method for chemically bonding a phenolic resin with a non-phenolic polymer (e.g., a synthetic fabric). The method comprises contacting a phenolic fatty acid compound with a non-phenolic polymer to introduce a hydroxy phenyl functional group into the non-phenolic polymer; and reacting the hydroxy phenyl functional group contained in the non-phenolic polymer with a phenolic resin or a phenolic crosslinker composition capable of forming a phenolic resin, to chemically bond the phenolic resin with the non-phenolic polymer. The invention is particularly useful for making a synthetic fabric-reinforced article, such as synthetic fabric-reinforced rubber article, circuit board substrate, or fiberglass.

Abstract: An aqueous ambient dry decorative or protective coating comprising a film forming matrix polymer of an aqueous emulsion polymer of aqueous copolymerized ethylenically unsaturated monomers modified with at least 3% by weight of a low molecular weight oligomer of copolymerized hydroxy alkanoic acid having 2 to 4 carbon atoms having a number average molecular weight between 300 and 10,000 to provide a film forming binder substantially free of volatile organic coalescing solvents. Preferred oligomers are homopolymers and copolymers of polymerized lactic acid or polymerized glycolic acid.