Abstract: A silane-grafted polyolefin composition is disclosed, and includes a desired reduced specific weight material. The composition finds application in a wide array of uses, and in particular automotive and uses such as weatherstrips, where this composition is used in place of conventional materials such as TPV and EPDM rubber formulations.

Abstract: An elastomeric article is provided that includes a composition having a silane-crosslinked polyolefin elastomer with a density less than 0.90 g/cm3. The elastomeric article can exhibit a compression set of from about 5.0% to about 35.0%, as measured according to ASTM D 395 (22 hrs @ 70° C.). The silane-crosslinked polyolefin elastomer can include a first polyolefin having a density less than 0.86 g/cm3, a second polyolefin having a crystallinity less than 40%, a silane crosslinker, a grafting initiator, and a condensation catalyst.

Abstract: A silane-grafted polyolefin composition is disclosed, and includes a desired reduced specific weight material. The composition finds application in a wide array of uses, and in particular automotive and uses such as hoses, where this composition is used in place of conventional materials such as TPV and EPDM rubber formulations.

Abstract: A silane-grafted polyolefin composition is disclosed, and includes a desired reduced specific weight material. The composition finds application in a wide array of uses, and in particular automotive and uses such as hoses, where this composition is used in place of conventional materials such as TPV and EPDM rubber formulations.

Abstract: A silane-grafted polyolefin composition is disclosed, and includes a desired reduced specific weight material. The composition finds application in a wide array of uses, and in particular automotive and uses such as weatherstrips, where this composition is used in place of conventional materials such as TPV and EPDM rubber formulations.

Abstract: A silane-grafted polyolefin composition is disclosed, and includes a desired reduced specific weight material. The composition finds application in a wide array of uses, and in particular automotive and uses such as hoses, where this composition is used in place of conventional materials such as TPV and EPDM rubber formulations.

Abstract: A silane-grafted polyolefin composition is disclosed, and includes a desired reduced specific weight material. The composition finds application in a wide array of uses, and in particular automotive and uses such as weatherstrips, where this composition is used in place of conventional materials such as TPV and EPDM rubber formulations.

Abstract: A silane-grafted polyolefin composition is disclosed, and includes a desired reduced specific weight material. The composition finds application in a wide array of uses, and in particular automotive and uses such as weatherstrips, where this composition is used in place of conventional materials such as TPV and EPDM rubber formulations.

Abstract: A static sealing member is provided that includes a composition having a silane-crosslinked polyolefin elastomer with a density less than 0.90 g/cm3. The static sealing member can exhibit a compression set of from about 5.0% to about 35.0%, as measured according to ASTM D 395 (22 hrs @ 70° C.). The silane-crosslinked polyolefin elastomer can include a first polyolefin having a density less than 0.86 g/cm3, a second polyolefin having a crystallinity less than 40%, a silane crosslinker, a grafting initiator, and a condensation catalyst.

Abstract: A roofing membrane and a method of making the same is provided. The roofing membrane includes a top layer having a flame retardant and a first silane-crosslinked polyolefin elastomer with a density less than 0.90 g/cm3; a scrim layer; and a bottom layer having a flame retardant and a second silane-crosslinked polyolefin elastomer with a density less than 0.90 g/cm3. The top and bottom layers of the roofing membrane both exhibit a compression set of from about 5.0% to about 35.0%, as measured according to ASTM D 395 (22 hrs @ 70° C.).

Abstract: A combined sealing member is provided that includes a composition comprising two or more polyolefin elastomers selected from the group consisting of a dense, a micro-dense and a dynamic silane-crosslinked polyolefin elastomer having a respective density of less than 0.90 g/cm3, less than 0.70 g/cm3, and less than 0.60 g/cm3. The combined sealing member exhibits a compression set of from about 5.0% to about 35.0%, as measured according to ASTM D 395 (22 hrs @ 70° C.).

Abstract: An elastomeric article is provided that includes a composition having a silane-crosslinked polyolefin elastomer with a density less than 0.90 g/cm3. The elastomeric article can exhibit a compression set of from about 5.0% to about 35.0%, as measured according to ASTM D 395 (22 hrs @70° C.). The silane-crosslinked polyolefin elastomer can include a first polyolefin having a density less than 0.86 g/cm3, a second polyolefin having a crystallinity less than 40%, a silane crosslinker, a grafting initiator, and a condensation catalyst.

Abstract: A microdense sealing member is provided. The microdense sealing member includes a composition having a foamed silane-crosslinked polyolefin elastomer with a density less than 0.70 g/cm3. The microdense sealing member can exhibit a compression set of from about 5.0% to about 35.0% measured according to ASTM D 395 (22 hrs @ 70° C.). The foamed silane-crosslinked polyolefin elastomer can be produced from a blend including a first polyolefin having a density less than 0.86 g/cm3, a second polyolefin having a crystallinity less than 60° C., a silane crosslinker, a grafting initiator, a condensation catalyst, and a microencapsulated foaming agent.

Abstract: A sponge sealing member is provided that includes a composition having a silane-crosslinked polyolefin elastomer with a density less than 0.60 g/cm3. The sponge sealing member can exhibit a compression set of from about 5.0% to about 35.0%, as measured according to ASTM D 395 (22 hrs @ 70° C.). The silane-crosslinked polyolefin elastomer can also include a first polyolefin having a density less than 0.86 g/cm3, a second polyolefin having a crystallinity less than 40%, a silane crosslinker, a grafting initiator, a condensation catalyst, and a foaming agent.

Abstract: A shoe sole composition and method for making a shoe sole are provided. The shoe sole includes a composition comprising a foamed silane-crosslinked polyolefin elastomer having a density less than 0.50 g/cm3. The shoe sole exhibits a compression set of from about 5.0% to about 20.0%, as measured according to ASTM D 395 (6 hrs @ 50° C.). The foamed silane-crosslinked polyolefin elastomer can be produced from a blend including a first polyolefin having a density less than 0.86 g/cm3, a second polyolefin, having a crystallinity less than 40%, a silane crosslinker, a grafting initiator, a condensation catalyst, and a foaming agent.

Abstract: A hose is provided. The hose has a composition including a silane-crosslinked polyolefin elastomer and a filler. The hose composition exhibits a compression set of from about 5% to about 35%, as measured according to ASTM D 395 Method B (168 hrs at 150 ° C.). The hose composition additionally has a density from about 0.88 g/cm3 to about 1.05 g/cm3. The hose may be used for transferring coolant liquid in a motor of a vehicle and includes a first outer layer of a first silane-crosslinked polyolefin elastomer; a second inner layer of a second silane-crosslinked polyolefin elastomer; and a textile reinforcement layer embedded between the first and second layers of the silane-crosslinked polyolefin elastomers.

Abstract: A hose made from a composition including one or more of EPR, EPDM, a silane-grafted polyolefin and a silicone-modified polyolefin; an one or more of fibers, polyamide powder, and ultra high molecular weight polyethylene powder. A hose comprising an outermost layer formed from a composition comprising: (A) at least one of EPR, EPDM, a silane-grafted polyolefin and a siliconemodified polyolefin; and (B) at least one of an ultra high molecular weight polyethylene powder, a polyamide powder, and fibers.