Abstract: The present invention relates to a process for preparing a catalyst which, in a formal sense, comprises 0.1 to 20% by mass of alkali metal and/or alkaline earth metal oxide, 0.1 to 99% by mass of oxide and 0.1 to 99% by mass of silicon dioxide, which is characterized in that it aluminum comprises the steps of treating an aluminosilicate with an aqueous alkali metal and/or alkaline earth metal salt solution under acidic conditions and calcining the aluminosilicate treated with aqueous alkali metal and/or alkaline earth metal salt solution, and to a catalyst which is obtainable by this process and, in a formal sense, comprises alkali metal and/or alkaline earth metal oxide, aluminum oxide and silicon dioxide, which is characterized in that the catalyst, in a formal sense, has a content of alkali metal and/or alkaline earth metal oxides of 0.

Abstract: A catalyst, useful in the preparation of isoolefins and containing 0.1 to 20% by mass of an alkali metal oxide, an alkaline earth metal oxide and mixtures thereof; 0.1 to 99% by mass of aluminum oxide; and 0.1 to 99% by mass of silicon dioxide, is prepared by a) treating an aluminosilicate with an aqueous alkali metal salt solution, an alkaline earth metal salt solution and mixtures thereof, under acidic conditions, to obtain a treated aluminosilicate; and b) calcining the treated aluminosilicate, to obtain the catalyst.

Abstract: A catalyst, useful in the preparation of isoolefins and containing 0.1 to 20% by mass of an alkali metal oxide, an alkaline earth metal oxide and mixtures thereof; 0.1 to 99% by mass of aluminum oxide; and 0.1 to 99% by mass of silicon dioxide, is prepared by a) treating an aluminosilicate with an aqueous alkali metal salt solution, an alkaline earth metal salt solution and mixtures thereof, under acidic conditions, to obtain a treated aluminosilicate; and b) calcining the treated aluminosilicate, to obtain the catalyst.

Abstract: A catalyst, useful in the preparation of isoolefins and containing 0.1 to 20% by mass of an alkali metal oxide, an alkaline earth metal oxide and mixtures thereof; 0.1 to 99% by mass of aluminum oxide; and 0.1 to 99% by mass of silicon dioxide, is prepared by a) treating an aluminosilicate with an aqueous alkali metal salt solution, an alkaline earth metal salt solution and mixtures thereof, under acidic conditions, to obtain a treated aluminosilicate; and b) calcining the treated aluminosilicate, to obtain the catalyst.

Abstract: A continuous process for preparing an isoolefin having 4 to 6 carbon atoms is performed by cleaving a compound of the formula I R1—O—R2 ??(I) wherein R1=a tertiary alkyl radical having 4 to 6 carbon atoms, and R2=H or an alkyl radical, in a gas phase over a solid catalyst, in the temperature range of 200 to 400° C., at a pressure of 0.1 to 1.2 MPa, in a reactor which is equipped with a heating jacket and is heated with a liquid heat carrier, wherein the cleavage is carried out in such a way that a temperature drop in the catalyst zone at any point in relation to the entrance temperature is less than 50° C., wherein (i) a reaction mixture in the reactor and (ii) the heat carrier in the jacket flow through the reactor in cocurrent, and wherein a temperature difference of the heat carrier between a feed point to the reactor and an outlet from the reactor is adjusted to less than 40° C.