Abstract: A method of producing a fully stabilized extra low carbon porcelain enameling steel having excellent formability and fish scaling resistance as well as superior enamel adherence. The method includes hot rolling a slab to strip, the slab having a composition consisting essentially of in weight percent: 0.005 max. C, 0.35 max. Mn, 0.015 max. P, 0.015 max. S, 0.015 max. Si, 0.025 to 0.055 Al, 0.006 to 0.015 N, 0.03 to 0.06 Ti, 0.02 to 0.05 Cb, up to 0.03 Sb, the balance Fe and inevitable impurities. The hot rolled strip is cold rolled at least 65% and box annealed until a cold spot temperature within the range of 610 to 705 degrees C. is reached. The invention includes the product made according to the process.