Abstract: An overcoat layer and method to make an overcoated photoconductor drum of an electrophotographic image forming device using irradiation such as with electron beam (EB) or ultraviolet (UV) light is provided. The photoconductor drum is then cured using EB dose of between 10 and 100 kiloGrays (kGy), preferably between 20 and 40 kGys or UV irradiation with an exposure of between 0.1 and 2 J/cm2. The unique overcoat layer of the present invention is formed having a biphasic morphology comprised of a highly cured crosslinked phase and a second phase enriched in uncured material. The desired amount of uncured uncrosslinked material found in the second phase of the biphasic structure, is between 2-70 wt % range, with particularly good combination of long-life and electrical performance when present at the 5-50 wt % level, and the best performance at the 15-40 wt % level.

Abstract: An overcoat layer and method to make an overcoated photoconductor drum of an electrophotographic image forming device using irradiation such as with electron beam (EB) or ultraviolet (UV) light is provided. The photoconductor drum is then cured using EB dose of between 10 and 100 kiloGrays (kGy), preferably between 20 and 40 kGys or UV irradiation with an exposure of between 0.1 and 2 J/cm2. The unique overcoat layer of the present invention is formed having a biphasic morphology comprised of a highly cured crosslinked phase and a second phase enriched in uncured material. The desired amount of uncured uncrosslinked material found in the second phase of the biphasic structure, is between 2-70 wt % range, with particularly good combination of long-life and electrical performance when present at the 5-50 wt % level, and the best performance at the 15-40 wt % level.

Abstract: An overcoat layer and method to make an overcoated photoconductor drum of an electrophotographic image forming device using irradiation such as with electron beam (EB) or ultraviolet (UV) light is provided. The photoconductor drum is then cured using EB dose of between 10 and 100 kiloGrays (kGy), preferably between 20 and 40 kGys or UV irradiation with an exposure of between 0.1 and 2 J/cm2. The unique overcoat layer of the present invention is formed having a biphasic morphology comprised of a highly cured crosslinked phase and a second phase enriched in uncured material. The desired amount of uncured uncrosslinked material found in the second phase of the biphasic structure, is between 2-70 wt % range, with particularly good combination of long-life and electrical performance when present at the 5-50 wt % level, and the best performance at the 15-40 wt % level.

Abstract: A method of quantifying the coverage of extra particulate additives (EPA) on the surface of toner particles is provided. More specifically, this invention is a method using automated image analysis to correctly identify toner and coverage of EPA particles on the surface of the toner.

Abstract: A method of quantifying the coverage of extra particulate additives (EPA) on the surface of toner particles is provided. More specifically, this invention is a method using automated image analysis to correctly identify toner and coverage of EPA particles on the surface of the toner.

Abstract: An overcoat layer and method to make an overcoated photoconductor drum of an electrophotographic image forming device using irradiation such as with electron beam (EB) or ultraviolet (UV) light is provided. The photoconductor drum is then cured using EB dose of between 10 and 100 kiloGrays (kGy), preferably between 20 and 40 kGys or UV irradiation with an exposure of between 0.1 and 2 J/cm2. The unique overcoat layer of the present invention is formed having a biphasic morphology comprised of a highly cured crosslinked phase and a second phase enriched in uncured material. The desired amount of uncured uncrosslinked material found in the second phase of the biphasic structure, is between 2-70 wt % range, with particularly good combination of long-life and electrical performance when present at the 5-50 wt % level, and the best performance at the 15-40 wt % level.

Abstract: An overcoat layer and method to make an overcoated photoconductor drum of an electrophotographic image forming device using irradiation such as with electron beam (EB) or ultraviolet (UV) light is provided. The photoconductor drum is then cured using EB dose of between 10 and 100 kiloGrays (kGy), preferably between 20 and 40 kGys or UV irradiation with an exposure of between 0.1 and 2 J/cm2. The unique overcoat layer of the present invention is formed having a biphasic morphology comprised of a highly cured crosslinked phase and a second phase enriched in uncured material. The desired amount of uncured uncrosslinked material found in the second phase of the biphasic structure, is between 2-70 wt % range, with particularly good combination of long-life and electrical performance when present at the 5-50 wt % level, and the best performance at the 15-40 wt % level.

Abstract: An overcoat layer and method to make an overcoated photoconductor drum of an electrophotographic image forming device using irradiation such as with electron beam (EB) or ultraviolet (UV) light is provided. The photoconductor drum is then cured using EB dose of between 10 and 100 kiloGrays (kGy), preferably between 20 and 40 kGys or UV irradiation with an exposure of between 0.1 and 2 J/cm2. The unique overcoat layer of the present invention is formed having a biphasic morphology comprised of a highly cured crosslinked phase and a second phase enriched in uncured material. The desired amount of uncured uncrosslinked material found in the second phase of the biphasic structure, is between 2-70 wt % range, with particularly good combination of long-life and electrical performance when present at the 5-50 wt % level, and the best performance at the 15-40 wt % level.