Abstract: Aqueous synthetic resin formulations essentially containA) from 3 to 75% by weight of one or more synthetic resins which are composed ofa) from 50 to 99.9% by weight of one or more unsaturated carboxylic or vinyl esters,b) from 0.1 to 12% by weight of one or more .alpha.,.beta.

Abstract: UV-crosslinkable materials based on (meth)acrylate copolymers contain copolymerized monomers of the general formula I ##STR1## where R is a certain alkyl radical, an aryl radical or a radical R.sup.1 and R.sup.1 is a radical ##STR2## where R.sup.2 to R.sup.6 are each H, alkyl, a non-ortho OH group, OCH.sub.3, OC.sub.2 H.sub.3, SH, SCH.sub.3, Cl, F, CN, COOH, COO(C.sub.1 -C.sub.3 -alkyl), CF.sub.3, N(CH.sub.3).sub.2, N(C.sub.2 H.sub.5).sub.2, N(CH.sub.3)C.sub.6 H.sub.5, .sup.+ N(CH.sub.3).sub.3 X.sup.- or .sup.+N(CH.sub.3).sub.X X.sup.-, where X.sup.- is an acid anion, and one or more of the radicals R.sup.2 to R.sup.

Abstract: This invention deals with novel copolymers having K values from 5 to 80 prepared by the radical polymerization of:(A) 20 to 80 weight percent, based on the total weight of (A) and (B), of at least one olefinic unsaturated polyoxyalkylene alcohol adduct or a polyester alcohol adduct;(B) 80 to 20 weight percent, based on the total weight of (A) and (B), of at least one vinyl monomer selected from the group consisting of N-vinylformamide, N-vinyl-2-pyrrolidone, N-vinyl-piperidone, N-vinyl-2-caprolactam, N-vinylimidazole, N-vinyl-2-ethylene-urea and N-vinyl-2-propylene-urea;(C) 0 to 40 parts by weight of glycidyl acrylate and/or glycidyl methacrylate;(D) 0 to 10 parts by weight of at least one .alpha.,.beta.-monoolefinic unsaturated acid; and(E) 0 to 30 parts by weight of at least one olefinic unsaturated carboxylic acid amide and or carboxylic acid ester and/or styrene;whereby the parts by weight of (C), (D) and (E) are each based on 100 parts by weight of monomers (A) and (B).

Abstract: Radiation-reactive mixtures suitable for producing insulating layers and printed circuits are composed of certain precursors for preparing polyimides, polyisoindoloquinazolinediones, polyoxiazinediones, polyquinazolinediones or polyquinazolones and aryl-containing carbonyl compounds which when excited by UV radiation are capable of hydrogen abstraction, these mixtures undergoing solubility differentiation on irradiation with actinic light.

Abstract: Copolymers which are curable by ultraviolet radiation in the air are prepared by a process in which a mixture of (A) from 80 to 99.9% by weight of olefinically unsaturated monomers, (B) from 0 to 10% by weight of a copolymerizable olefinically unsaturated, photoreactive compound which, in the excited state produced by UV radiation, is capable of abstracting hydrogen and (C) from 0 to 10% by weight of a polymerization-regulating photoreactive compound which, in the excited state, is capable of abstracting hydrogen is subjected to free radical polymerization, the sum of (B) and (C) being not less than 0.1% by weight and the stated percentages by weight being based on the sum of the weights of (A)+(B)+(C).

Abstract: This invention deals with novel copolymers having K values of from 5 to 80 prepared by the radical polymerization of:(A) 20 to 80 weight percent, based on the total weight of (A) and (B), of at least one olefinic unsaturated polyoxyalkylene alcohol adduct or a polyester alcohol adduct;(B) 80 to 20 weight percent, based on the total weight of (A) and (B), of at least one vinyl monomer selected from the group consisting of N-vinylformamide, N-vinyl-2-pyrrolidone, N-vinyl-piperidone, N-vinyl-2-caprolactam, N-vinylimidazole, N-vinyl-2-ethylene-urea and N-vinyl-2-propylene-urea;(C) 0.05 to 40 parts by weight of glycidyl acrylate and/or glycidyl methacrylate;(D) 0 to 10 parts by weight of at least one .alpha.,.beta.-monoolefinic unsaturated acid; and(E) 0 to 30 parts by weight of at least one olefinic unsaturated carboxylic acid amide and or carboxylic acid ester and/or styrene;whereby the parts by weight of (C), (D) and (E) are each based on 100 parts by weight of monomers (A) and (B).

Abstract: Hotmelt contact adhesives which are crosslinkable with UV light in the air are based on copolymers which contain tetrahydrofurfur-2-yl (meth)acrylate and/or N-2-tetrahydrofurfuryl (meth)-acrylamide and/or alkoxyalkyl (meth)acrylates and/or N-alkoxyalkyl (meth)acrylamides as copolymerized units and added benzophenone and/or benzophenone derivatives as photosensitizers.

Abstract: Materials which are cross-linkable by ultraviolet radiation under atmospheric oxygen and are based on (meth)acrylate copolymers having a K value of from 10 to 100 are obtained by free radical polymerization, in the presence or absence of a solvent, ofa) from 5% to 97.4% by weight of isoamyl acrylate and/or isoamyl methacrylate,b) from 9% to 89.9% by weight of (methacrylates whose homopolymers have a glass transition temperature below -30.degree. C.,c) from 2.5% to 30% by weight of .alpha.,.beta.-monoolefinically unsaturated compounds whose homopolymers have a glass transition temperature above -30.degree. C.,d) from 0% to 10% by weight of monoolefinically unsaturated acids and/or their anhydrides ande) from 0% to 20% by weight of further olefinically unsaturated monomers having one or more of the following functional groups: hydroxyl, amide, epoxide, ether, ester, urethane, urea, primary, secondary and tertiary amine and ether groups, andf) from 0.

Abstract: Radiation-crosslinkable contact adhesive mixtures are prepared from polymers having a glass transition temperature of less than 0.degree. C. and a K value of from 20 to 80, derivatives of dihydroxypropyl (meth)acrylates as reactive diluents and small amounts of polymerizable tertiary amino compounds by a process in which the mixture is heated at from 80.degree. to 120.degree. C. for not more than 2 hours and solvents are then separated off under atmospheric or reduced pressure.

Abstract: Efflorescence phenomena on mineral substrates are prevented by coating the surface of the mineral substrates with aqueous polyacrylate dispersions and drying the coating, if necessary at elevated temperatures, by a process in which a mixture of(A) a dispersion of a copolymer of(a) (meth)acrylates of alkanols which are of 3 to 20 carbon atoms and have a tertiary CH group,(b) styrene, .alpha.-methylstyrene, methyl methacrylate, tert-butyl (meth)acrylate and/or (meth)acrylonitrile and(c) mono- and/or dicarboxylic acids of 3 to 5 carbon atoms and/or or their amides which may be substituted at the N atom by alkyl, and(B) an aromatic ketoneis used for the coating, and the coating is exposed to ultraviolet light.

Abstract: Polymers in bead form are prepared from water-soluble ethylenically unsaturated monomers by a reverse suspension polymerization of a liquid in the presence of polymerization initiators and protective colloids obtainable by grafting polymers (A) containing (a) aromatic monovinyl monome from 40 to 100% by weight (b) C.sub.3-6 monoethylenically unsaturated carboxylic acid and/or maleic anhydride from 0 to 60% by weight (c) other monoethylenically unsaturated monomers from 0-20% by weight, as copolymerized units with the proviso that the sum of the weight (a) to (c) is always 100 and the polymer (A) has a molecular weight (number average) from 500 to 20,000 and a hydrogenation iodine number from 1.3 to 51 with a fixed monomer mixture at given concentration levels.

Abstract: Epoxy resin materials essentially contain(A) an epoxy resin having a mean molecular weight of from 300 to 6,000 and on average from 1.5 to 3.0 epoxy groups in the molecule and(B) a polyacrylate resin obtainable by polymerization of essentially(b.sub.1) from 30 to 95% by weight of esters of acrylic acid and/or methacrylic acid and/or ethylacrylic acid with C.sub.1 -C.sub.20 -alcohols in the presence of(b.sub.2) from 5 to 70% by weight of carboxyl-containing copolymers having a mean molecular weight of from 500 to 20,000, obtainable by bulk or solution polymerizationand are used for heat-curable finishes, adhesive bonds and coatings.

Abstract: Nonaqueous polymer dispersions are obtainable by polymerization of esters (A) of acrylic acid and/or methacrylic acid and/or ethylacrylic acid with C.sub.1 -C.sub.20 -alcohols in an organic solvent or a mixture of organic solvents in which the polymers formed are insoluble, and in the presence of copolymers (B) having a molecular weight of from 500 to 20,000 and obtainable by bulk or solution polymerization of monoolefinically unsaturated monomers at from 180.degree. to 400.degree. C. and from 1 to 200 bar, and the said dispersions are used for the production of finishes, coating materials and adhesives.

Abstract: Paper and paperboard of high dry strength are produced by adding a dry strength enhancer to the paper stock and dewatering the paper stock with sheet formation by using as the dry strength enhancer a mixture of a cationic polymer which contains as characteristic monomers copolymerized units of(a) diallyldimethylammonium chloride,(b) N-vinylamine or(c) a substituted or unsubstituted N-vinylimidazoline and has a K value of not less than 30, and natural potato starch which is converted into a water-soluble form by heating in an aqueous medium at above the gelatinization temperature of natural potato starch in the absence of any oxidizing agents or alkali.

Abstract: Crosslinkable polymeric compositions which are dissolved or dispersed in an organic solvent, a process for their preparation and their use.These polymeric compositions which undergo crosslinking at room temperature or elevated temperatures after drying are obtained by reacting polymeric organic compounds containing carbonyl groups with polyhydrazides in the presence of monoketones or monoaldehydes.They are useful as crosslinking agents for polyepoxide compounds.