Abstract: In order to attain as low a final temperature as possible after as short a period of time as possible in a method of cooling hot briquetted sponge iron (3) under optimum utilization of the cooling medium, the hot briquetted sponge iron (3), in a first cooling step (11), is passed exclusively by a gaseous cooling medium while being gently cooled and subsequently, in a second cooling step (14), is sprayed with a liquid cooling medium, thus being intensively cooled to the final temperature desired.

Abstract: In a process for the direct reduction of iron-oxide containing material, synthesis gas is mixed with top gas formed in the direct reduction of the iron-oxide containing material and is used as a reducing gas for direct reduction. In order to avoid metal dusting despite an elevated CO-content of the reducing gas, or to reduce metal dusting, in a procedurally simple and cost-saving manner while minimizing the energy demand, an H.sub.2 O content of between 1 and 2%, preferably amounting to about 1.5%, is achieved in the reducing gas by subjecting a partial volume of the top gas to CO.sub.2 scrubbing prior to being used as a reducing gas, wherein the top gas subjected to CO.sub.2 scrubbing is mixed with the synthesis gas, is brought to a predetermined temperature by direct water irrigation while being saturated with H.sub.2 O, after direct water irrigation is heated to a temperature above the saturation temperature by admixing CO.sub.2 -unscrubbed top gas, and subsequently is used as a reducing gas.

Abstract: With a process for the direct reduction of particulate iron-containing material by fluidization, reformed gas, at least partially freed from CO.sub.2, is supplied to a fluidized-bed reduction zone as a reducing gas and is carried off from the same as a top gas and at least a portion of the top gas together with reformed gas is utilized for direction reduction. To economize on parts of the plant that are impinged on by reducing gas and in order to achieve savings in terms of heating costs, CH.sub.4 and N.sub.2 are, in addition to CO.sub.2, at least partially removed by adsorption, from 50 to 100% of the reformed as and 0 to 100% of the top gas, and the tail gas removed from the reformed gas and/or the top gas by adsorption is utilized as a heating gas.