Abstract: Method for manufacturing sintered oxidic nuclear fuel bodies by molding uranium oxide starting powder, a mixture of uranium oxide and plutonium oxide starting powder or of uranium-plutonium oxide mixed-crystal starting powder to form blanks and by a heat treatment of these blanks with a U.sub.4 O.sub.9 or (U, Pu).sub.4 O.sub.9 crystal phase developed in them to a degree which can be crystallographically detected at a sintering temperature in the range of 1000.degree. to 1400.degree. C. in an oxidizing and subsequently in a reducing gas atmosphere. The starting powder and/or the blanks are preroasted at a roasting temperature below the sintering temperature in a roasting gas atmosphere with oxidizing action and with an oxygen potential in which the U.sub.4 O.sub.9 (U, Pu).sub.4 O.sub.9 crystal phase is developed and cooled down subsequently to a starting temperature below the roasting temperature in an inert or oxidizing cooling-down gas atmosphere.

Abstract: Method for the manufacture of oxidic nuclear fuel bodies by a heat treatment of blanks obtained from UO.sub.2 starting power or a mixture of UO.sub.2 and PuO.sub.2 starting powder at a treatment temperature in the range of 1000.degree. C. to 1400.degree. initially in a gas atmosphere with oxidizing action and subsequently in a gas atmosphere with reducing action. The oxygen potential of the gas atmosphere with oxidizing action is kept in a range in which a crystallographically demonstrable U.sub.4 O.sub.9 or (U, Pu).sub.4 O.sub.9 crystal phase is generated in the blanks during the heating to the treatment temperature in this gas atmosphere with oxidizing action.

Abstract: Manufacture of oxidic nuclear fuel bodies with oxygen-to-metal ratio of 2.0.+-.0.02 at relatively low sintering temperature in range of 1000.degree.-1400.degree. C. Nuclear fuel powder with an arbitrary oxygen-to-metal ratio is mixed with a grain-growth promoting additive (U.sub.3 O.sub.8) and pressed into blanks. The blanks are subjected to a two-stage operation in a furnace at 1000.degree.-1400.degree. C. - an oxidative-sintering stage in a carbon dioxide atmosphere and a reducing stage in a hydrogen containing atmosphere.