Abstract: A peroxide-crosslinkable composition comprising: (A) A peroxide-crosslinkable polymer, e.g., a polyethylene; (B) A nitrogenous base, e.g., a low molecular weight, or low melting, or liquid nitrogenous base such as triallyl cyanurate (TAC); and (C) One or more antioxidants (AO), e.g., distearylthiodipropionate (DSTDP). The composition is useful in the manufacture of insulation sheaths for high and extra high voltage wire and cable.

Abstract: The process for making extra high voltage cable insulation is improved by using a composition comprising in weight percent based on the weight of the composition: (A) 95 to 99.9% of an ethylene-based polymer; (B) 0.2 to 2.5% peroxide; (C) 0.01 to 0.5% of a sulfur-containing first antioxidant having at least one —S(CH2)2CO2R group, wherein R is C6 to C20 alkyl; (D) 0.001 to 0.009%) of a sulfur-containing second antioxidant that does not contain a —S(CH2)2CO2R group, wherein R is a C6 to C20 alkyl; (E) Optionally, an organic nitrogenous base; and (F) Optionally, a phenolic third antioxidant that does not contain a —S(CH2)2CO2R group, wherein R is a C6 to C20 alkyl.

Abstract: A peroxide-crosslinkable composition comprising: (A) A peroxide-crosslinkable polymer, e.g., a polyethylene; (B) A nitrogenous base, e.g., a low molecular weight, or low melting, or liquid nitrogenous base such as triallyl cyanurate (TAC); and (C) One or more antioxidants (AO), e.g., distearylthiodipropionate (DSTDP). The composition is useful in the manufacture of insulation sheaths for high and extra high voltage wire and cable.

Abstract: A peroxide-crosslinkable composition comprising: (A) A peroxide-crosslinkable polymer, e.g., a polyethylene; (B) A nitrogenous base, e.g., a low molecular weight, or low melting, or liquid nitrogenous base such as triallyl cyanurate (TAC); and (C) One or more antioxidants (AO), e.g., distearylthiodipropionate (DSTDP). The composition is useful in the manufacture of insulation sheaths for high and extra high voltage wire and cable.

Abstract: The process for making extra high voltage cable insulation is improved by using a composition comprising in weight percent based on the weight of the composition: (A) 95 to 99.9% of an ethylene-based polymer; (B) 0.2 to 2.5% peroxide; (C) 0.01 NI to 0.5% of a sulfur-containing first antioxidant having at least one —S(CH2)2CO2R group, wherein R is a C6 to C20 alkyl; (D) 0.001 to 0.009%) of a phosphorus-containing second antioxidant that does not contain a —S(CH2)2C02R group, wherein R is a C6 to C20 alkyl; (E) Optionally, an organic nitrogenous base; and (F) Optionally, a phenolic third antioxidant that does not contain a —S(CH2)2C02R group, wherein R is a C6 to C20 alkyl.

Abstract: The process for making extra high voltage cable insulation is improved by using a composition comprising in weight percent based on the weight of the composition: (A) 95 to 99.9% of an ethylene-based polymer; (B) 0.2 to 2.5% peroxide; (C) 0.01 to 0.5% of a sulfur-containing first antioxidant having at least one —S(CH2)2C02R group, wherein R is C6 to C20 alkyl; (D) 0.001 to 0.009%) of a sulfur-containing second antioxidant that does not contain a —S(CH2)2C02R group, wherein R is a C6 to C20 alkyl; (E) Optionally, an organic nitrogenous base; and (F) Optionally, a phenolic third antioxidant that does not contain a —S(CH2)2C02R group, wherein R is a C6 to C20 alkyl.

Abstract: The process for making extra high voltage cable insulation is improved by using a composition comprising in weight percent based on the weight of the composition: (A) 95 to 99.9% of an ethylene-based polymer; (B) 0.2 to 2.5% peroxide; (C) 0.01 NI to 0.5% of a sulfur-containing first antioxidant having at least one —S(CH2)2CO2R group, wherein R is a C6 to C20 alkyl; (D) 0.001 to 0.009%) of a phosphorus-containing second antioxidant that does not contain a —S(CH2)2C02R group, wherein R is a C6 to C20 alkyl; (E) Optionally, an organic nitrogenous base; and (F) Optionally, a phenolic third antioxidant that does not contain a —S(CH2)2C02R group, wherein R is a C6 to C20 alkyl.

Abstract: Highly-mineral-filled, halogen-free, flame-retardant compositions made from or containing a polypropylene thermoplastic elastomer, a polypropylene, a metal hydroxide filler, and a polar-monomer-grafted polyolefin elastomer compatibilizer. Such compositions can be employed in preparing various articles of manufacture, including extruded articles and coated conductors, such as cables.

Abstract: The present invention is a highly mineral-filled halogen-free, flame-retardant composition made from or containing a mineral filler, an olefin multi-block interpolymer, and a polar-monomer-based compatibilizer. The invented system has improved elongation at break, achieves a highly flexible, soft compound at high (e.g. >40 weight percent) filler addition, and achieves and low residual deformation when subjected to the hot pressure test. The invention also includes cables and extruded articles prepared from the composition.

Abstract: The present invention is a highly mineral-filled halogen-free, flame-retardant composition made from or containing a polypropylene thermoplastic elastomer, a polypropylene, a metal hydroxide filler, and a polar-monomer-grafted polyolefin elastomer compatibilizer. The invented system has improved tensile strength, improved elongation at break, and low permanent deformation at increasingly high test temperatures. The invention also includes cables and extruded articles prepared from the composition.

Abstract: This invention relates to a flame-retardant composition useful for preparing a coated automotive wire with high scrape abrasion resistance and flexibility. The present invention is a halogen-free, flame-retardant composition made from or containing an ethylene/alpha-olefin copolymer, a halogen-free inorganic flame retardant, a coupling agent for coupling the inorganic flame retardant to the copolymer, and a processing aid.