Abstract: A stable emulsion comprising a polyetherimide resin, neutralization agent, cosolvent, solvent, ring opening agent, and water, for use in a cataphoretic deposition process for forming a polyetherimide coating on a substrate, particularly a substrate having a complex geometry.

Abstract: A thermoplastic resin composition comprises units represented by the amide formula (I): ##STR1## and the ester formula (II): ##STR2## wherein said amide units are present as a physical mixture in said resin or as a polymer with the repeating ester units to impart an enhanced crystallization rate as compared to said resin without said amide units of formula (I), said amide units being present in an effective amount to decrease the difference between the temperature of melting and the temperature of crystallization of said resin to an amount less than 5 mole percent of amide unites of formula (I) based on the moles of ester units of formula (II).

Abstract: The present invention deals with the distribution of polyphenylene ethers 1. by reacting the polyphenylene ether in solution with a phenolic compound, wherein special phenolic compounds are used. The redistribution reaction can be performed in toluene or in toluene/alcohol blends. The reaction can be run in the presence or the absence of a catalyst.

Abstract: A method of recovering dihydric phenol, particularly bisphenol-A, from compositions containing the reaction residue of bisphenol-A units which method comprises:a. granulating a bisphenol-A containing polymer;b. treating the particles with an alcohol, or any other organic swelling solvent miscible with water and easily distilled off from an aqueous solution, preferably a C.sub.1 -C.sub.10 alcohol for a time sufficient to swell the particles;c. contacting the swelled particles with a ammoniacal solution at a temperature of at least about 25.degree. C. depending on the swelling solvent employed in order to selectively sever the ester bonds of the bisphenol-A residue units;d. separating the liquid phase from the solid phase;e. distilling ammonia and swelling solvent from the liquid phase of d. above, thus obtaining an essentially aqueous solution with dissolved urea and partially precipitated bisphenol-A;f. adding sufficient water to the residue of e.