Abstract: The present disclosure relates to a healable superplastic amorphous alloy, and specifically, to a healable superplastic amorphous alloy capable of exhibiting superplastic behavior and unique healable behavior by maximizing the complexity of the amorphous structure for an Icosahedral quenched-in nuclei quasi-crystal cluster to be formed in the amorphous matrix through the composition limitation and additive element control of Zr—Cu—Ni—Al alloy.

Abstract: Disclosed are a wire rod and a manufacturing method therefor. The wire rod comprises in percentage by weight: 0.02 to 0.15% of C; 0.05 to 0.3% of Si; 0.5 to 1.2% of Mn; 0.3 to 0.9% of Cr; 0.02% or less of P; 0.02% or less of S; 0.01 to 0.05% of sol. Al; 0.01% or less of N; Fe as the remainder; and unavoidable impurities, wherein the wire rod satisfies following formulas 1 and 2, wherein, when the hardness of the wire rod measured in 1/2d position and in 1/4d position in the diameter direction of the wire rod is Hv,1/2d(Hv) and Hv,1/4d(Hv), respectively (here, d is the diameter of the wire). (Hv,1/2d+Hv,1/4d)/2?150??[Formula 1] Hv,1/2d/Hv,1/4d?1.

Abstract: Disclosed are a wire rod and a manufacturing method therefor. The wire rod comprises in percentage by weight: 0.02 to 0.15% of C; 0.05 to 0.3% of Si; 0.5 to 1.2% of Mn; 0.3 to 0.9% of Cr; 0.02% or less of P; 0.02% or less of S; 0.01 to 0.05% of sol. A1; 0.01% or less of N; Fe as the remainder; and unavoidable impurities, wherein the wire rod satisfies following formulas 1 and 2, wherein, when the hardness of the wire rod measured in 1/2d position and in 1/4d position in the diameter direction of the wire rod is Hv,1/2d(Hv) and Hv,1/4d(Hv), respectively (here, d is the diameter of the wire). [Formula 1] (Hv,1/2d+Hv,1/4d)/2?150 [Formula 2] Hv,1/2d/Hv,1/4d?1.

Abstract: There are provided a steel wire rod for ultra-high-strength parts such as automobile engine bolts or structural mechanical parts, and a method for producing the steel wire rod. The steel wire rod having high strength and ductility includes, by wt %, carbon (C): 0.7% to 0.9%, manganese (Mn): 13% to 17%, copper (Cu): 1% to 3%, and the balance of iron (Fe) and inevitable impurities.

Abstract: Provided is a wire rod having enhanced strength and impact toughness comprising, by wt %, carbon (C): 0.05% to 0.15%, silicon (Si): 0.2% or less, manganese (Mn): 3.0% to 4.0%, phosphorus (P): 0.020% or less, sulfur (5):0.020% or less, boron (B): 0.0010% to 0.0030%, titanium (Ti): 0.010% to 0.030%, nitrogen (N): 0.0050% or less, aluminum (Al): 0.010% to 0.050%, iron (Fe) as a residual component thereof, and other unavoidable impurities. A microstructure includes bainitic ferrite in an area fraction of 90% or more, and a martensite/austenite (M/A) constituent as a residual component thereof.

Abstract: There are provided a steel wire rod for ultra-high-strength parts such as automobile engine bolts or structural mechanical parts, and a method for producing the steel wire rod. The steel wire rod having high strength and ductility includes, by wt %, carbon (C): 0.7% to 0.9%, manganese (Mn): 13% to 17%, copper (Cu): 1% to 3%, and the balance of iron (Fe) and inevitable impurities.

Abstract: The present invention relates to a wire rod used in bolts for automobile engines, for example, and more specifically to a wire rod having an improved resistance to hydrogen delayed fracture, to a manufacturing method for same, to a bolt using same and a method for manufacturing the bolt. Provided are a high strength wire rod having a superior resistance to hydrogen delayed fracture and a method for manufacturing same, a high strength bolt using the wire rod and a method for manufacturing same, wherein. the wire rod comprises, 0.3-0.7 wt % C, 0.05-2.0 wt % Si, 0.7-1.5 wt % Mn, 0.01-0.1 wt % Ni, and 30-70 ppm La, and the remainder thereof is comprised by Fe and inevitable impurities.