Abstract: In one embodiment, a chalcogenide glass optical fiber is produced by forming a billet including a chalcogenide glass mass and a polymer mass in a stacked configuration, heating the billet to a temperature below the melting point of the chalcogenide glass, extruding the billet in the ambient environment to form a preform rod having a chalcogenide glass core and a polymer jacket, and drawing the preform rod.

Abstract: A fiber is provided, including a cladding material that is disposed along a longitudinal-axis fiber length. A plurality of spherical particles are disposed as a sequence along a longitudinal line parallel to the longitudinal fiber axis in at least a portion of the fiber length, and include a spherical particle material that is interior to the fiber cladding material and different than the fiber cladding material. To produce particles, a drawn fiber, having a longitudinal-axis fiber length and including at least one fiber core that has a longitudinal core axis parallel to the longitudinal fiber axis and that is internally disposed to at least one outer fiber cladding layer along the fiber length, is heated for a time that is sufficient to cause a fiber core to break-up into droplets sequentially disposed along the fiber core axis. Fiber cooling solidifies droplets into spherical particles interior to fiber cladding.

Abstract: There is provided a fiber including a cladding material that is disposed along a longitudinal-axis fiber length. A plurality of spherical particles are provided, separated from one another and disposed in a longitudinal line parallel to the longitudinal fiber axis. The particles are in a sequence with controlled periodic spacing between particles along at least a portion of the fiber length. Each spherical particle has a spherical particle material that is embedded within and elementally different than the fiber cladding material.

Abstract: In one embodiment, a chalcogenide glass optical fiber is produced by forming a billet including a chalcogenide glass mass and a polymer mass in a stacked configuration, heating the billet to a temperature below the melting point of the chalcogenide glass, extruding the billet in the ambient environment to form a preform rod having a chalcogenide glass core and a polymer jacket, and drawing the preform rod.

Abstract: In one embodiment, a chalcogenide glass optical fiber is produced by forming a billet including a chalcogenide glass mass and a polymer mass in a stacked configuration, heating the billet to a temperature below the melting point of the chalcogenide glass, extruding the billet in the ambient environment to form a preform rod having a chalcogenide glass core and a polymer jacket, and drawing the preform rod.

Abstract: A fiber is provided, including a cladding material that is disposed along a longitudinal-axis fiber length. A plurality of spherical particles are disposed as a sequence along a longitudinal line parallel to the longitudinal fiber axis in at least a portion of the fiber length. Each spherical particle is of a spherical particle material that is interior to and different than the fiber cladding material. The spacing between adjacent spherical particles in the sequence of particles is greater than the spherical particle diameter. Each spherical particle can be provided as a core-shell particle that includes a spherical core that is surrounded by at least one spherical shell. Each spherical particle can be provided with a plurality of azimuthal sections of at least two distinct materials.

Abstract: In one embodiment, a chalcogenide glass optical fiber is produced by forming a billet including a chalcogenide glass mass and a polymer mass in a stacked configuration, heating the billet to a temperature below the melting point of the chalcogenide glass, extruding the billet in the ambient environment to form a preform rod having a chalcogenide glass core and a polymer jacket, and drawing the preform rod.