Abstract: A sulphoaluminate clinker includes as a phasic formulation, compared with the total weight of clinker: 5 to 25% of a calcium aluminoferrite phase with a formulation corresponding to the general formula C2AXF(1?X), with X comprised between 0.2 and 0.8; 15 to 35% of a calcium sulphoaluminate phase yee' limit (C4A3$); 40 to 75% belite (C2S); from 0.01 to 10% of one or several minor phases selected from the group consisting of calcium sulphates, alkali sulphates, perovskite, calcium aluminates, gehlenite, free lime and periclase, and/or a vitreous phase, and additives including at least sodium and boron present in the following quantities, by weight as compared to the total weight of the clinker: from 0.1 to 5% of sodium expressed as sodium oxide and from 0.2 to 3% of boron, expressed as boron oxide, the total content of said additives being less than or equal to 15%.

Abstract: A sulphoaluminate clinker includes as a phasic formulation, compared with the total weight of clinker: 5 to 25% of a calcium aluminoferrite phase with a formulation corresponding to the general formula C2AXF(1?X), with X comprised between 0.2 and 0.8; 15 to 35% of a calcium sulphoaluminate phase yee' limit (C4A3$); 40 to 75% belite (C2S); from 0.01 to 10% of one or several minor phases selected from the group consisting of calcium sulphates, alkali sulphates, perovskite, calcium aluminates, gehlenite, free lime and periclase, and/or a vitreous phase, and additives including at least sodium and boron present in the following quantities, by weight as compared to the total weight of the clinker: from 0.1 to 5% of sodium expressed as sodium oxide and from 0.2 to 3% of boron, expressed as boron oxide, the total content of said additives being less than or equal to 15%.

Abstract: The present invention concerns a belite-rich sulphoaluminous clinker, a method for producing such a clinker and its use for preparing hydraulic binders, and comprising as a mineralogical formulation: 5 to 25%, preferably 10 to 20%, of a calcium aluminoferrite phase with a formulation corresponding to the general formula C2AXF(1?X), with X comprised between 0.2 and 0.8. 15 to 35%, preferably 20 to 30%, of a calcium sulphoaluminate phase “yee' limit” (C4A3$), 40 to 75%, preferably 45 to 65% belite (C2S), from 0.01 to 10% of one or several minor phases selected from calcium sulphates, alkaline sulphates, perovskite, calcium aluminates, gehlenite, free limestone and periclase, and/or a vitreous phase, and at least one or several secondary elements selected from sulphur, magnesium, sodium, potassium, boron, phosphorus, zinc, manganese, titanium, fluorine, chlorine, the total content of these secondary elements being less than or equal to 15%.

Abstract: The present invention relates to a method of preparing a hydraulic binder wherein at least the following two binders are mixed together: a) a first hydraulic binder having as one of its main components the mineral compound C4A3{overscore (S)}; and b) a sulfate second binder based on calcium sulfate hemihydrate and/or anhydrite obtained by applying heat treatment to gypsum. The present invention also provides a binder comprising amongst its main components: a) a mineral compound C4A3{overscore (S)}; and b) a compound comprising a hemihydrate of calcium sulfate of &agr; or &bgr; form and of general formula CaSO4, ½H2O and/or an anhydrite of III form of general formula CaSO4, &egr;H2O with &egr; lying in the range 0 to 0.5, preferably in the range 0.06 to 0.11, or an anhydrite of II form of formula CaSO4.