Abstract: The preparation of objects, in particular optical components and/or devices, is described using, as precursors of optical materials, amorphous monolithic aerogels for high-precision mechanical machining.

Abstract: A method for preparing inorganic oxide-based materials of spherical form with substantially monomodal distribution, consisting of forming a sol of at least one of the inorganic oxides of interest, adding to said sol a solvent immiscible with the sol, finely dispersing the obtained two-phase mixture into a dispersion of particles of equal diameter, growing said particles by limited coalescence to the desired diameter, gelling said mixture by adding a second solvent containing a gelling agent, and removing the solvent.

Abstract: Microbeads of aerogels of one or more oxides are characterised by a high porosity and the fact that at least 90% of the pores present have a diameter lying within a very narrow range. The surface area exceeds 300 m.sup.2 /g and more frequently exceeds 500 m.sup.2 /g, the total pore volume exceeding 1 ml/g.

Abstract: A method for preparing inorganic oxide-based materials of spherical form with substantially monomodal distribution, consisting of forming a sol of at least one of the inorganic oxides of interest, adding to said sol a solvent immiscible with the sol, finely dispersing the obtained two-phase mixture into a dispersion of particles of equal diameter, growing said particles by limited coalescence to the desired diameter, gelling said mixture by adding a second solvent containing a gelling agent, and removing the solvent.

Abstract: The invention relates to high-porosity silica xerogels and a process for their preparation consisting of subjecting silica alcogels to thermal treatment in the presence of organic compounds containing amino and hydroxyl groups.The xerogels are characterised by a total pore volume .gtoreq.2 cc/g and a mean pore diameter .gtoreq.100 .ANG..

Abstract: A process for the preparation of monoliths of aerogels of metal oxides, which aerogel is either constituted by one single oxide, or is constituted by a mixture of oxides, is disclosed, which process consists of the following operating steps:(a) the relevant metal alkoxide(s) is/are mixed with water in the presence of a catalyst of acidic character;(b) the so obtained mixture is hydrolysed;(c) a colloidal suspension of the oxide of a metal equal to, or different from, the metal(s) used in the (a) step is added to the hydrolysate;(d) the so obtained colloidal solution is caused to turn into a gel (gelation) having the desired shape and dimensions;(e) the gel is washed;(f) the gel is dried at values of temperature and pressure which are higher than the critical pressure and temperature values of the solvent used for the washing.

Abstract: Ceramic pellets, which may have, or not, nuclear fuel materials embedded therein, are formed by first preparing a gel by precipitation of metallic salts from solutions of their compounds at a concentration of at least 10 grams per liter, said solutions being added dropwise to a coagulation bath which contains, for example, ammonium or sodium hydroxide, whereafter the precipitated gel are fired, in one or two stages, to precondition them prior to the compaction to form the final pellets which are subsequently sintered at an appropriate temperature.