Abstract: A binding fiber having, as at least one first thermoplastic component, a copolyamide which has a relative viscosity of at least 1.50 (measured at 0.5% in m-cresol at 25° C.), a MVR of maximum 20 cm3/10 min at 190° C. and 2.16 kg load, a hydrophobicity of less than 7.2, a melting temperature lower than 105° C. in the water saturated condition and a higher melting temperature in the dry condition. The binding fiber can, on the one hand, be activated with hot steam at approximately ambient pressure during the manufacture of flat materials containing natural fibers, such as paper, cardboard, wood fiber boards, or fiber mats. The finished flat material can, on the other hand, be subjected to higher temperatures, and the copolyamide develops good bonding with respect to the cellulose fibers normally used in the indicated flat materials.

Abstract: A binding fiber having, as at least one first thermoplastic component, a copolyamide which has a relative viscosity of at least 1.50 (measured at 0.5% in m-cresol at 25° C.), a MVR of maximum 20 cm3/10 min at 190° C. and 2.16 kg load, a hydrophobicity of less than 7.2, a melting temperature lower than 105° C. in the water saturated condition and a higher melting temperature in the dry condition. The binding fiber can, on the one hand, be activated with hot steam at approximately ambient pressure during the manufacture of flat materials containing natural fibers, such as paper, cardboard, wood fiber boards, or fiber mats. The finished flat material can, on the other hand, be subjected to higher temperatures, and the copolyamide develops good bonding with respect to the cellulose fibers normally used in the indicated flat materials.

Abstract: In a core-shroud bicomponent fiber, which exhibits a core and a shroud at least partially enveloping the core, an elevated abrasion behavior, a low compaction under exposure to temperature and pressure and a high strength of the fibers is achieved by having the shroud consist of 45-98% w/w of a first polyamide having a melting point exceeding 280° C., and 2-20% w/w of a layer silicate.

Abstract: A method for self-crimping of S/S bi-component fibers on a fiber line includes the steps of main drawing, post-drawing on a cold drawing unit, water application in the tensed state and relaxation at the dryer inlet in the compact closed state, which results in fibers with a novel .OMEGA.-shaped crimping structure.