Abstract: This disclosure provides an aging process or a method for aging aluminum alloys. For example, the aging process can be performed on 6xxx Al-Si-Mg-Cu aluminum alloys to result in production of such alloys with improved intergranular corrosion (IGC) resistance. The disclosed aging process includes subjecting a solution heat treated and quenched 6xxx aluminum alloy to a temperature above an aging hardening temperature of said alloy but below the solution heat treatment temperature for a short period of time, and then subjecting said alloy to an aging heat treatment at an aging hardening temperature.

Abstract: A method of producing an aluminium alloy brazing sheet for the manufacturing of light brazed assemblies, wherein said brazing sheet has good formability, combined with a low susceptibility to core penetration in the end annealed as-produced condition after stretching, forming and/or shaping and brazing are disclosed. Assemblies made according to the method are also disclosed.

Abstract: A method of producing an aluminium alloy brazing sheet for the manufacturing of light brazed assemblies, wherein said brazing sheet has good formability, combined with a low susceptibility to core penetration in the end annealed as-produced condition after stretching, forming and/or shaping and brazing are disclosed. Assemblies made according to the method are also disclosed.