Abstract: A composite bipolar plate for a polymer electrolyte membrane fuel cell (PEMFC) is prepared as follows: a) compounding vinyl ester and graphite powder to form bulk molding compound (BMC) material, the graphite powder content ranging from 60 wt % to 95 wt % based on the total weight of the graphite powder and vinyl ester, wherein carbon fiber 1-20 wt %, modified organo clay or noble metal plated modified organo clay 0.5-10 wt %, and one or more conductive fillers selected form: carbon nanotube (CNT) 0.1-5 wt %, nickel plated carbon fiber 0.5-10 wt %, nickel plated graphite 2.5-40 wt %, and carbon black 2-30 wt %, based on the weight of the vinyl ester resin, are added during the compounding; b) molding the BMC material from step a) to form a bipolar plate having a desired shaped at 80-200° C. and 500-4000 psi.

Abstract: The present invention discloses a polymer blend of sulfonated polymer such as poly(ether ether ketone) and poly(amide imide) for use as an proton-conducting membrane. The poly(amide imide) is prepared by conducing a ring-opening and condensation reactions of diisocyanate and 1,2,4-benzenetricarboxylic anhydride (TMA). The polymer blend has a reduced methanol uptake and methanol permeability while maintaining good proton conductivity, and thus is suitable for use as a proton-conducting membrane of a fuel cell. The present invention also discloses a process for preparing the poly(amide imide).

Abstract: A composite bipolar plate for a polymer electrolyte membrane fuel cell (PEMFC) is prepared as follows: a) compounding vinyl ester and graphite powder to form bulk molding compound (BMC) material, the graphite powder content ranging from 60 wt % to 95 wt % based on the total weight of the graphite powder and vinyl ester, wherein carbon fiber 1-20 wt %, modified organo clay or noble metal plated modified organo clay 0.5-10 wt %, and one or more conductive fillers selected form: carbon nanotube (CNT) 0.1-5 wt %, nickel plated carbon fiber 0.5-10 wt %, nickel plated graphite 2.5-40 wt %, and carbon black 2-30 wt %, based on the weight of the vinyl ester resin, are added during the compounding; b) molding the BMC material from step a) to form a bipolar plate having a desired shaped at 80-200° C. and 500-4000 psi.