Abstract: A high strength cold rolled steel sheet having excellent burring properties includes: by weight %, 0.13-0.25% of carbon (C), 1.0-2.0% of silicon (Si), 1.5-3.0% of manganese (Mn), 0.08-1.5% of aluminum (Al)+chrome (Cr)+molybdenum (Mo), 0.1% or less of phosphorus (P), 0.01% or less of sulfur (S), 0.01% or less of nitrogen (N), and the balance of Fe and inevitable impurities; and, by area fraction, 3-25% of ferrite, 20-40% of martensite, 5-20% of residual austenite. The ferrite has an average grain size of 2 ?m or less at the reference point of 4/t (wherein t refers to a steel sheet thickness), with the average ratio between lengths in the thickness direction and in the rolling direction being 1.5 or less.

Abstract: A high-strength cold-rolled steel sheet having excellent bending workability includes, by weight %, 0.13-0.25% of carbon (C), 1.0-2.0% of silicon (Si), 1.5-3.0% of manganese (Mn), 0.08-1.5% of aluminum (Al)+chromium (Cr)+molybdenum (Mo), 0.1% or less of phosphorus (P), 0.01% or less of sulfur (S), 0.01% or less of nitrogen (N), the remainder of Fe and inevitable impurities, and comprises, by area fraction, 3-25% of ferrite, 20-40% of martensite, and 5-20% of retained austenite, in which a nickel-rich layer formed of nickel (Ni) introduced from the outside is provided on a surface layer portion, and the concentration of nickel (Ni) at a depth of 1 ?m from the surface may be greater than or equal to 0.15 wt %.

Abstract: Provided are a high-strength cold-rolled steel sheet and a hot-dip galvanized steel sheet comprising in % by weight: 0.05 to 0.3% of carbon (C); 0.6 to 2.5% of silicon (Si); 0.01 to 0.5% of aluminum (Al); 1.5 to 3.0% of manganese (Mn); and the remainder being Fe and unavoidable impurities, the steel sheet has a microstructure comprised of, in an area fraction, ferrite in an amount of 60% or less, lath-type bainite of 25% or more, martensite of 5% or more, and lath-type retained austenite in an amount of 5%, wherein the ferrite has an average grain diameter of 2 ?m or less and the ferrite satisfies Fn2, defined by relational expression 1, is 89% or more and Fa5, defined by relational expression 2, is 70% or less.

Abstract: Provided are a high strength cold rolled steel plate having excellent yield strength, ductility, and hole expandability, a hot dip galvanized steel plate, and a method for producing the same. The cold rolled steel plate of the present invention comprises 0.06-0.2 wt % of carbon (C), 1.5-3.0 wt % of manganese (Mn), 0.3-2.5 wt % of silicon (Si), 0.01-0.2 wt % of aluminum (Al), 0.01-3.0 wt % of nickel (Ni), 0.2 wt % or less of molybdenum (Mo), 0.01-0.05 wt % of titanium (Ti), 0.02-0.05 wt % of antimony (Sb), 0.0005-0.003 wt % of boron (B), 0.01 wt % or less (but not 0%) of nitrogen (N), with the remainder comprising Fe and unavoidable impurities, and the microstructure thereof comprises, in terms of area fraction, 50% or more of bainite, 10% or more of tempered martensite (TM), 10% or less of fresh martensite (FM), 20% or less of residual austenite, and 5% or less of ferrite.

Abstract: Provided is a method of continuously annealing a strip. The method includes: firstly heating a strip in a first heating zone; firstly cooling the firstly heated strip or maintaining the firstly heated strip at a constant temperature in a first cooling or constant temperature maintaining zone; secondarily heating and soaking the strip, firstly cooled or remaining at the constant temperature, in a second heating and soaking zone; and secondarily cooling the strip, secondarily heated and soaked, in a second cooling zone.

Abstract: Provided is a method of continuously annealing a strip. The method includes: firstly heating a strip in a first heating zone; firstly cooling the firstly heated strip or maintaining the firstly heated strip at a constant temperature in a first cooling or constant temperature maintaining zone; secondarily heating and soaking the strip, firstly cooled or remaining at the constant temperature, in a second heating and soaking zone; and secondarily cooling the strip, secondarily heated and soaked, in a second cooling zone.

Abstract: The present invention relates to an apparatus for continuous annealing of a strip, capable of manufacturing a high-strength and highly ductile cold-rolled steel sheet having both excellent strength and ductility, and to a method for continuous annealing of a strip. The continuous annealing apparatus, according to the present invention, is capable of continuous annealing by cooling after heating, and then reheating, unlike an existing continuous annealing apparatus which heats only once and then cools or provides an overaging treatment. As a result, the continuous annealing apparatus, according to the present invention, can preliminarily render a homogeneous texture or control the texture as desired, and then perform another reheating heat treatment to stabilize the texture or control the shape thereof to a desired state.

Abstract: Provided are a high-strength cold-rolled steel sheet and a hot-dip galvanized steel sheet comprising in % by weight: 0.05 to 0.3% of carbon (C); 0.6 to 2.5% of silicon (Si); 0.01 to 0.5% of aluminum (Al); 1.5 to 3.0% of manganese (Mn); and the remainder being Fe and unavoidable impurities, the steel sheet has a microstructure comprised of, in an area fraction, ferrite in an amount of 60% or less, lath-type bainite of 25% or more, martensite of 5% or more, and lath-type retained austenite in an amount of 5%, wherein the ferrite has an average grain diameter of 2 ?m or less and the ferrite satisfies Fn2, defined by relational expression 1, is 89% or more and Fa5, defined by relational expression 2, is 70% or less.

Abstract: An apparatus for continuous annealing of a strip comprises: a first heating zone configured to firstly heat a strip; a first cooling or constant temperature maintaining zone configured to cool the strip firstly heated in the first heating zone or to maintain the strip at a constant temperature; a second heating and soaking zone configured to secondarily heat and soak the strip cooled or remaining at the constant temperature in the first cooling or constant temperature maintaining zone; and a second cooling zone configured to cool the strip heated and soaked in the second heating and soaking zone.

Abstract: A steel sheet for enameling for eliminating surface defects such as fish scale defects and having excellent formability, and provides a steel sheet for enamel having no surface defects, including: more than 0 wt % and 0.005 wt % or less of C, 0.1 to 0.5 wt % of Mn, more than 0 wt % and 0.03 wt % or less of Si, 0.05 to 0.3 wt % of Cr, more than 0 wt % and 0.03 wt % or less of Al, 0.03 to 0.1 wt % of O, more than 0 wt % and 0.03 wt % or less of P, more than 0 wt % and 0.02 wt % or less of S, more than 0 wt % and 0.015 wt % or less of Cu, more than 0 wt % and 0.005 wt % or less of N, Fe in a remaining content, and other inevitable impurities.

Abstract: A steel sheet for enameling for eliminating surface defects such as fish scale defects and having excellent formability, and provides a steel sheet for enamel having no surface defects, including: more than 0 wt % and 0.005 wt % or less of C, 0.1 to 0.5 wt % of Mn, more than 0 wt % and 0.03 wt % or less of Si, 0.05 to 0.3 wt % of Cr, more than 0 wt % and 0.03 wt % or less of Al, 0.03 to 0.1 wt % of O, more than 0 wt % and 0.03 wt % or less of P, more than 0 wt % and 0.02 wt % or less of S, more than 0 wt % and 0.015 wt % or less of Cu, more than 0 wt % and 0.005 wt % or less of N, Fe in a remaining content, and other inevitable impurities.