Abstract: Mixed metal oxide catalysts having an amorphous content of not less than 40 wt. % are prepared by calcining the catalyst precursor fully or partially enclosed by a porous material having a melting temperature greater than 600° C. in an inert container including heating the catalyst precursor at a rate from 0.5 to 10° C. per minute from room temperature to a temperature from 370° C. to 540° C. under a stream of pre heated gas chosen from steam and inert gas and mixtures thereof at a pressure of greater than or equal to 1 psig having a temperature from 300° C. to 540° C. and holding the catalyst precursor at that temperature for at least 2 hours and cooling the catalyst precursor to room temperature.

Abstract: Mixed metal oxide catalysts having an amorphous content of not less than 40 wt. % are prepared by calcining the catalyst precursor fully or partially enclosed by a porous material having a melting temperature greater than 600° C. in an inert container including heating the catalyst precursor at a rate from 0.5 to 10° C. per minute from room temperature to a temperature from 370° C. to 540° C. under a stream of pre heated gas chosen from steam and inert gas and mixtures thereof at a pressure of greater than or equal to 1 psig having a temperature from 300° C. to 540° C. and holding the catalyst precursor at that temperature for at least 2 hours and cooling the catalyst precursor to room temperature.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining and treating the resulting catalyst with the equivalent amount of peroxide after calcining.

Abstract: Mixed metal oxide catalysts having an amorphous content of not less than 40 wt. % are prepared by calcining the catalyst precursor fully or partially enclosed by a porous material having a melting temperature greater than 600° C. in an inert container including heating the catalyst precursor at a rate from 0.5 to 10° C. per minute from room temperature to a temperature from 370° C. to 540° C. under a stream of pre heated gas chosen from steam and inert gas and mixtures thereof at a pressure of greater than or equal to 1 psig having a temperature from 300° C. to 540° C. and holding the catalyst precursor at that temperature for at least 2 hours and cooling the catalyst precursor to room temperature.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining.

Abstract: Mixed metal oxide catalysts having an amorphous content of not less than 40 wt. % are prepared by calcining the catalyst precursor fully or partially enclosed by a porous material having a melting temperature greater than 600° C. in an inert container including heating the catalyst precursor at a rate from 0.5 to 10° C. per minute from room temperature to a temperature from 370° C. to 540° C. under a stream of pre heated gas chosen from steam and inert gas and mixtures thereof at a pressure of greater than or equal to 1 psig having a temperature from 300° C. to 540° C. and holding the catalyst precursor at that temperature for at least 2 hours and cooling the catalyst precursor to room temperature.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining.

Abstract: A process for preparing an oxidative dehydrogenation catalyst or oxidative dehydrogenation catalyst precursor that includes mixing solutions of molybdenum and tellurium at a pH from about 3.3 to 7.5; adjusting the pH of the resulting solution back to about 5 and adding VOSO4 and adding a solution of Nb2O5 and oxalic acid and treating the resulting precursor slurry in a controlled pressure hydrothermal process to obtain the catalyst.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining.

Abstract: The preparation of an oxidative dehydrogenation catalyst comprising Mo, V, Nb and Te using a hydrothermal step the activity and reproducibility of the catalyst is improved by conduction the hydrothermal step at higher pressures while permitting gaseous products to leave the reactor. In some instances a condenser may be upstream of the pressure relief valve.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining and treating the resulting catalyst with the equivalent amount of peroxide after calcining.

Abstract: Mixed metal oxide catalysts having an amorphous content of not less than 40 wt. % are prepared by calcining the catalyst precursor fully or partially enclosed by a porous material having a melting temperature greater than 600° C. in an inert container including heating the catalyst precursor at a rate from 0.5 to 10° C. per minute from room temperature to a temperature from 370° C. to 540° C. under a stream of pre heated gas chosen from steam and inert gas and mixtures thereof at a pressure of greater than or equal to 1 psig having a temperature from 300° C. to 540° C. and holding the catalyst precursor at that temperature for at least 2 hours and cooling the catalyst precursor to room temperature.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining and treating the resulting catalyst with the equivalent amount of peroxide after calcining.

Abstract: A process for preparing an oxidative dehydrogenation catalyst or oxidative dehydrogenation catalyst precursor that includes mixing solutions of molybdenum and tellurium at a pH from about 3.3 to 7.5; adjusting the pH of the resulting solution back to about 5 and adding VOSO4 and adding a solution of Nb2O5 and oxalic acid and treating the resulting precursor slurry in a controlled pressure hydrothermal process to obtain the catalyst.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining and treating the resulting catalyst with the equivalent amount of peroxide after calcining.

Abstract: The preparation of an oxidative dehydrogenation catalyst comprising Mo, V, Nb and Te using a hydrothermal step the activity and reproducibility of the catalyst is improved by conduction the hydrothermal step at higher pressures while permitting gaseous products to leave the reactor. In some instances a condenser may be upstream of the pressure relief valve.

Abstract: Oxidative dehydrogenation catalysts comprising MoVNbTeO having improved consistency of composition and a 25% conversion of ethylene at less than 420° C. and a selectivity to ethylene above 95% are prepared by treating the catalyst precursor with H2O2 in an amount equivalent to 0.30-2.8 mL H2O2 of a 30% solution per gram of catalyst precursor prior to calcining.