Abstract: The present invention is to a molded rigid polyurethane foam for application in appliance, having a reduced thermal conductivity at densities between 33 and 38 kg/m3 and a process for the production of such foams. The molded rigid polyurethane foam have a ratio of applied foam density (kg/m3) to lambda (mW/mK), measured at 10° C., 24 hours after foam production from 1.65 and to 2.15 and are obtained by the process of injecting into a closed mold cavity under reduced pressure a reaction mixture at a packing factor of 1.1 to 1.9 and the reaction mixture comprises: A) an organic polyisocyanate; B) a physical blowing agent, C) a polyol composition containing at least one polyol with a functionality of 3 or greater and a hydroxyl number between 200 and 800 and a water content of 0 to 2.5 weight percent of the total polyol composition; D) catalyst and E) auxiliary substances and/or additives.

Abstract: The present invention is to a molded rigid polyurethane foam for application in appliance, having a reduced thermal conductivity at densities between 33 and 38 kg/m3 and a process for the production of such foams. The molded rigid polyurethane foam have a ratio of applied foam density (kg/m3) to lambda (mW/mK), measured at 10° C., 24 hours after foam production from 1.65 and to 2.15 and are obtained by the process of injecting into a closed mold cavity under reduced pressure a reaction mixture at a packing factor of 1.1 to 1.9 and the reaction mixture comprises: A) an organic polyisocyanate; B) a physical blowing agent, C) a polyol composition containing at least one polyol with a functionality of 3 or greater and a hydroxyl number between 200 and 800 and a water content of 0 to 2.5 weight percent of the total polyol composition; D) catalyst and E) auxiliary substances and/or additives.

Abstract: A process is disclosed for preparing an open-celled rigid polyurethane foam by reacting an organic polyisocyanate with a polyol in the presence of a blowing agent, a cell opening agent and exfoliating graphite, wherein the thermal conductivity of the foam is from 28 to 35 mw/mk. Such foams are applicable in the construction industry where it is desired to have a foam having flame retardation properties and a low thermal conductivity.

Abstract: A method for producing an open cell low-density semi-rigid polyurethane foam suitable for general use as a thermal insulating material and/or an acoustical applications is disclosed. The method comprises a method for producing a flame-retardant open-celled semi-rigid polyurethane foam having an overall density of 5 to 30 kg/m2 by reacting (a) a polyisocyanate and (b) a polyol having a molecular weight of 100 to 10,000, in the presence of (c) an effective amount of an exfoliating graphite, (d) blowing agent and (e) optional additional auxiliary substances to produce.