Abstract: The present invention relates to electrodeposition material for the electrochemical deposition of a corrosion-protective layer of TiO2 on an electrically conductive substrate comprising a titanium compound, a complexing agent, an accelerator, water and optionally organic solvents, buffering agents and one or more additives, characterized in that the titanium compound is titanyl sulfate and/or titanyl oxalate, the complexing agent is selected from the group consisting of citric acid, citrates, tartaric acid, tartrates, lactic acid, lactates, gluconic acid, gluconates, polyhydroxy-polycarbonic acids, ethylenediaminetetraacetate, methylglycinediacetate, iminodisuccinate, nitrilotriacetic acid and nitrilotriacetate, triethanolamine, phosphonic acid and phosphonates, polyaspartic acid and polyaspartates, polyacrylic acid and polyacrylates and the accelerator is selected from the group consisting of H2O2 and organic peroxides.

Abstract: An oral and dental hygiene product is comprised of a composite material comprising calcium salts which are slightly soluble in water, in the form of nanoparticulate primary particles having a length of from 5 to 150 nm and a cross section of from 2 to 50 nm and protein components selected from the group consisting of proteins, protein hydrolysates and protein hydrolysate derivatives, and 0.1 to 9% by weight of a cleaning agent based on the total weight of the product.

Abstract: The invention relates to compositions for treating tooth and/or bone tissue that contain calcium phosphates, calcium fluorides or calcium fluorophosphates, all of which being poorly soluble in water, and polyelectrolytes. The compositions can be cured and are suited for the smoothing, the reconstruction, and the remineralizing treatment of tooth and bone tissue, especially for eliminating microroughnesses.

Abstract: The invention relates to a method for producing a suspension of an undecomposed meltable material having an average particle diameter of between 5 to 500 nm. The inventive method enables stable suspensions to be produced and is characterised in that it only requires a simple technical infrastructure in many production plants, it delivers high space-time yields, and can easily be scaled up.

Abstract: A cosmetic or pharmaceutical composition used for blocking the penetration of ultraviolet radiation, the composition containing nanoscale organic UV filters having a mean diameter of from 10 to 300 nm.

Abstract: The invention relates to the use of nanoscale sterols and/or sterol esters with particle diameters of 10 to 300 nm as food additives and as active substances for the production of hypocholesterolemic agents. The particular fineness of the particles promotes more rapid absorption by the blood serum after oral ingestion by comparison with conventional sterols and sterol esters.

Abstract: The invention relates to sodium silicates with a modulus (molar ratio of SiO.sub.2 to Na.sub.2 O) of 1.3 to 4 in the form of a fine-particle solid in shard-like form or compounds containing these silicates with the ability to reduce incrustation when used as a builder component in detergents. These useful materials are distinguished in particular by the fact that they are in the form of an X-ray amorphous overdried material (primary drying product) with water contents below 15% by weight and apparent densities of the non-compacted solid granules of 500 g/l or lower which has been produced by drying of a water-containing sodium silicate preparation using a hot gas phase as the drying medium and/or by heating of a spray-dried sodium silicate with water contents of at least 15% by weight at temperatures of 120.degree.to 450.degree. C., if necessary accompanied or followed by the application of forces to produce the shard-like structure.

Abstract: Method for producing alkali metal silicates from crystalline siliceous material and aqueous alkali metal hydroxide solution at high temperature and normal pressure, characterized in that cristobalite and/or tempered quartz sand are used as the siliceous material, and this material is reacted with aqueous, 20 to 50 wt. % sodium or potassium hydroxide solution at temperatures of 100.degree. to 150.degree. C. and normal pressure, the molar ratio of SiO.sub.2 to Na.sub.2 O or K.sub.2 O in the reaction mixture being between 2:1 and 1:7.

Abstract: Synthetic swellable layer silicates corresponding to the following formulaMgO.aMA.bAl.sub.2 O.sub.3.cSiO.sub.2.nH.sub.2 O (I)in whichM is Na.sup.+ and Li.sup.+ having an Na:Li ratio of at least 1;A is F.sup.-, OH.sup.- or 1/2O.sup.2- or a mixture thereof;a is 0.1 to 0.6;b is 0 to 0.3;c is 1.2 to 1.7; andn is 0 to 3.0.are used in water-based well-servicing fluids as a high-temperature-stable thixotrope substantially unaffected by alkaline earth metal ions.