Abstract: The present invention relates to polysiloxane nanoparticles having the following properties: an average particle size d50 (measured using REM recordings) in the range of 10-200 nm, a specific surface area Ao of at least 50 m2/g, a pore volume of at least 0.2 cm3/g, an average pore volume d50 of at least 0.8 nm, wherein the particles have groups that contain carbon, which groups are bonded to the silicon at least partially in the form of unsubstituted or substituted alkyl, alkenyl, aryl, arylalkyl, or alkylaryl groups.

Abstract: The present invention relates to polysiloxane nanoparticles have the following properties: an average particle size d50 (measured using REM recordings) in the range of 10-200 nm, a specific surface area Ao of at least 50 m2/g, a pore volume of at least 0.2 cm3/g, an average pore volume d50 of at least 0.8 mn, whereas the particles have groups that contain carbon, which groups are bonded to the silicon at least partially in the form of unsubstituted or substituted alkyl, alkenyl, aryl, arylalkyl, or alkylaryl groups.

Abstract: The present invention relates to a composition containing silico-organic nanohybrid and/or microhybrid capsules for scratch-resistant and/or abrasion-resistant coatings, wherein the silico-organic nanohybrid and/or microhybrid system includes one or more small metal oxide cores A and a substantially complete, silico-organic shell B, and the composition can be obtained by a reaction performed in situ, in a synthetic resin or in a synthetic-resin precursor compound, between metal oxide particles (KA-O) and at least one organofunctional silicon compound which contains an organofunctional group and at least one hydrolyzable group or at least one hydroxy group. The present invention also relates to the use of such compositions as the base for lacquers for producing a scratch-resistant and abrasion-resistant coating on a substrate as well as articles provided with corresponding scratch-resistant as well as abrasion-resistant coatings.

Abstract: High-temperature resistant polymerizable metal oxide particles having a glass transition temperature of the homopolymerizable ≧100° C. and a core A. The core includes an oxide of a metal or semimetal of the third to sixth main group, of the first to eighth subgroup of the periodic table, or of the lanthanides, and has at least one group —(B)w—X bound via the oxygen atom of the oxide or hydroxide, in which B represents a binding link, and X represents a reactive functional group, and w is equal to 0 or 1. The inventive particles are useful, in particular, for producing coating materials, molding materials and adhesives.

Abstract: Organosilicon nano/microhybrid systems or microhybrid systems having nanoscale and/or microscale oxide particles (KA—O), and an organosilicon shell with at least one organosilicon constituent of the general formula Ia wherein the organosilicon constituent of the shell B is attached to the oxide particles via one or more covalent linkages of formula Ib A process for preparing a composition comprising organosilicon nano/microhybrid systems or microhybrid systems directly in a synthetic resin composition allows in situ preparation of a curable resin. The compositions may be used as coating materials for producing scratch resistant and abrasion resistant coatings.

Abstract: The invention relates to a stratified material with a coating which is deposited on one side or both sides and which is comprised of a planar substrate containing acrylate. The synthetic resin is modified by means of high-temperature resistant, polymerizable nanoparticles having a glass transition temperature of the homopolymerizates ≧150 ° C. Said nanoparticles comprise a core consisting of silicon dioxide and of at least one side chain which is covalently bound to the core via one or several oxygen atoms of the oxide, and which is of the formula (MeO)x(Me—(CH2)n—(OCO)m—CR1═CH2)y, wherein Me represents Si or Al, x is 1 to 3, m is 0 and 1, n is 0 to 6, y is 1 to 3 and R represents H or CH3, whereby the free valences of Me represent a binding to another oxygen atom of the core or are saturated by alkoxy radicals.

Abstract: The present invention relates to a composition containing silico-organic nanohybrid and/or microhybrid capsules for scratch-resistant and/or abrasion-resistant coatings, wherein the silico-organic nanohybrid and/or microhybrid system includes one or more small metal oxide cores A and a substantially complete, silico-organic shell B, and the composition can be obtained by a reaction performed in situ, in a synthetic resin or in a synthetic-resin precursor compound, between metal oxide particles (KA—O) and at least one organofunctional silicon compound which contains an organofunctional group and at least one hydrolyzable group or at least one hydroxy group. The present invention also relates to the use of such compositions as the base for lacquers for producing a scratch-resistant and abrasion-resistant coating on a substrate as well as articles provided with corresponding scratch-resistant as well as abrasion-resistant coatings.

Abstract: Organosilicon nano/microhybrid systems or microhybrid systems having nanoscale and/or microscale oxide particles (KA—O), and an organosilicon shell with at least one organosilicon constituent of the general formula Ia 1