Abstract: A method of making polymeric, e.g., polyester, filaments having low denier spread by use of a polymer of high viscosity is described. The filaments are useful to make yarns and other articles.

Abstract: Polyester filaments of high shrinkage and high shrinkage tension may be prepared by heat treatment of undrawn crystalline filaments of low shrinkage and shrinkage tension, and may be used for making polyester yarns of mixed shrinkage and bulky polyester yarns and fabrics therefrom.

Abstract: Polyester mixed fine filament yarns having excellent mechanical quality and uniformity, and preferably with a balance of good dyeability and shrinkage, are prepared by a simplified direct spin-orientation process by selection of polymer and spinning conditions.

Abstract: Polyester fine filaments having excellent mechanical quality and uniformity, and preferably with a balance of good dyeability and shrinkage, are prepared by a simplified direct spin-orientation process by selection of polymer viscosity and spinning conditions, followed by drawing and/or bulking.

Abstract: Polyester filaments of high shrinkage and high shrinkage tension may be prepared by heat treatment of undrawn crystalline filaments of low shrinkage and shrinkage tension, and may be used for making polyester yarns of mixed shrinkage and bulky polyester yarns and fabrics therefrom.

Abstract: Polyester fine filaments having excellent mechanical quality and uniformity, and preferably with a balance of good dyeability and shrinkage, are prepared by a simplified direct spin-orientation process by selection of polymer viscosity and spinning conditions.

Abstract: Polyester fine filaments having excellent mechanical quality and uniformity, and preferably with a balance of good dyeability and shrinkage, are prepared by a simplified direct spin-orientation process by selection of polymer viscosity and spinning conditions.

Abstract: A process of making mixed shrinkage yarn, including drawing, especially cold-drawing, or hot-drawing or other heat-treatments of spin-oriented crystalline polyester filaments, and particularly polyester feed yarns, that have been prepared by spinning at speeds of, e.g., 4 km/min, and have low shrinkage and no natural draw ratio in the conventional sense, that provides useful technique for obtaining uniform drawn filaments of desired denier and of differential shrinkage, and thereby provides improved flexibility to obtain filaments and yarns of mixed shrinkage.

Abstract: Poly(ethylene terephthalate) filaments of enhanced dyeability, low boil-off shrinkage (even in as-spun condition), good thermal stability over a large temperature range; and useful as texturing feed yarns and/or as hard yarns requiring no further drawing are prepared by spinning at extremely high speeds, and are characterized by a long period spacing above 300 A in their as-spun condition, and, whether in as-spun condition or after heat-treatment, by a low skin-core value as measured by a differential birefringence in relation to their stress measured at 20% extension (which correlates approximately with the spinning speed), a large crystal size, and low amorphous orientation. The continuous filament yarns may be draw-textured to provide textured yarns which also show enhanced dyeability. The staple fiber yarns also have very useful properties as compared with conventional staple yarns.

Abstract: Poly(ethylene terephthalate) filaments of enhanced dyeability, low boil-off shrinkage (even in as-spun condition), good thermal stability over a large temperature range, and useful as texturing feed yarns and/or as hard yarns requiring no further drawing are prepared by spinning at extremely high speeds, and are characterized by a long period spacing above 300 A in their as-spun condition, and, whether in as-spun condition or after heat-treatment, by a low skin-core value as measured by a differential birefringence in relation to their stress measured at 20% extension (which correlates approximately with the spinning speed), a large crystal size, and low amorphous orientation. The continuous filament yarns may be draw-textured to provide textured yarns which also show enhanced dyeability. The staple fiber yarns also have very useful properties as compared with conventional staple yarns.