Abstract: A method for forming a substantially oxygen-free silicon carbide layer on a substrate, where the silicon carbide layer has a dielectric constant of less than about four. The substrate is held at a deposition temperature of between about zero centigrade and about one hundred centigrade, and a gas flow of tetramethylsilane is introduced at a rate of no more than about one thousand scientific cubic centimeters per minute. The deposition pressure is held between about one milli Torr and about one hundred Torr, and a radio frequency plasma discharge is produced with a power of no more than about two kilowatts. The plasma discharge is halted when a desired thickness of the silicon carbide layer has been formed.

Abstract: A method for forming a substantially oxygen-free silicon carbide layer on a substrate, where the silicon carbide layer has a dielectric constant of less than about four. The substrate is held at a deposition temperature of between about zero centigrade and about one hundred centigrade, and a gas flow of tetramethylsilane is introduced at a rate of no more than about one thousand scientific cubic centimeters per minute. The deposition pressure is held between about one milli Torr and about one hundred Torr, and a radio frequency plasma discharge is produced with a power of no more than about two kilowatts. The plasma discharge is halted when a desired thickness of the silicon carbide layer has been formed.

Abstract: A method for forming a substantially oxygen-free silicon carbide layer on a substrate, where the silicon carbide layer has a dielectric constant of less than about four. The substrate is held at a deposition temperature of between about zero centigrade and about one hundred centigrade, and a gas flow of tetramethylsilane is introduced at a rate of no more than about one thousand scientific cubic centimeters per minute. The deposition pressure is held between about one milli Torr and about one hundred Torr, and a radio frequency plasma discharge is produced with a power of no more than about two kilowatts. The plasma discharge is halted when a desired thickness of the silicon carbide layer has been formed.

Abstract: A method of forming a planarized layer on a substrate, where the substrate is cleaned, and the layer is formed having a surface with high portions and low portions. A resistive mask is formed over the low portions of the layer, but not over the high portions of the layer. The surface of the layer is etched, where the high portions of the layer are exposed to the etch, but the low portions of the layer underlying the resistive mask are not exposed to the etch. The etch of the surface of the layer is continued until the high portions of the layer are at substantially the same level as the low portions of the layer, thereby providing an initial planarization of the surface of the layer. The resistive mask is removed from the surface of the layer, and all of the surface of the layer is planarized to provide a planarized layer.