Abstract: A core crush resistant prepreg for use in making a fiber reinforced composite panel structure is provided. The prepreg comprises a woven fabric consisting essentially of carbon fiber tow strands impregnated with a hardenable polymeric resin composition. Typically the fabric has an areal weight of from about 180 to about 205 grams per square meter. The prepreg has an average fiber tow aspect ratio of less than about 15.4, a prepreg thickness of at least about 0.245 mm, and a prepreg openness of at least about 1.2 percent but less than about 6.0 percent. Preferably, the resin composition is predominantly viscous in nature and has a tan &dgr; value of between 0.9 and 2.0 at an elevated temperature between 70° C. and 140° C., and an average epoxy functionality of greater than 2.0. A method for evaluating core crush resistance properties of a prepreg is also provided.

Abstract: A core crush resistant prepreg for use in making a fiber reinforced composite panel structure is provided. The prepreg comprises a woven fabric consisting essentially of carbon fiber tow strands impregnated with a hardenable polymeric resin composition. Typically the fabric has an areal weight of from about 180 to about 205 grams per square meter. The prepreg has an average fiber tow aspect ratio of less than about 15.4, a prepreg thickness of at least about 0.245 mm, and a prepreg openness of at least about 1.2 percent but less than about 6.0 percent. Preferably, the resin composition is predominantly viscous in nature and has a tan &dgr; value of between 0.9 and 2.0 at an elevated temperature between 70° C. and 140° C., and an average epoxy functionality of greater than 2.0. A method for evaluating core crush resistance properties of a prepreg is also provided.

Abstract: A core crush resistant prepreg for use in making a fiber reinforced composite panel structure is provided. The prepreg comprises a woven fabric consisting essentially of carbon fiber tow strands impregnated with a hardenable polymeric resin composition. Typically the fabric has an areal weight of from about 180 to about 205 grams per square meter. The prepreg has an average fiber tow aspect ratio of less than about 15.4, a prepreg thickness of at least about 0.245 mm, and a prepreg openness of at least about 1.2 percent but less than about 6.0 percent. Preferably, the resin composition is predominantly viscous in nature and has a tan &dgr; value of between 0.9 and 2.0 at an elevated temperature between 70° C. and 140° C., and an average epoxy functionality of greater than 2.0. A method for evaluating core crush resistance properties of a prepreg is also provided.

Abstract: A core crush resistant prepreg for use in making a fiber reinforced composite panel structure is provided. The prepreg comprises a woven fabric consisting essentially of carbon fiber tow strands impregnated with a hardenable polymeric resin composition. Typically the fabric has an areal weight of from about 180 to about 205 grams per square meter. The prepreg has an average fiber tow aspect ratio of less than about 15.4, a prepreg thickness of at least about 0.245 mm, and a prepreg openness of at least about 1.2 percent but less than about 6.0 percent. Preferably, the resin composition is predominantly viscous in nature and has a tan &dgr; value of between 0.9 and 2.0 at an elevated temperature between 70° C. and 140° C., and an average epoxy functionality of greater than 2.0. A method for evaluating core crush resistance properties of a prepreg is also provided.