Abstract: A method for preparing a supported catalyst, including mixing waste lithium battery cathode material and biomass uniformly to obtain a mixture, then putting the mixture into a tube furnace for nitrogen purging, and then heating and calcining to obtain a solid sample after carbothermal reduction treatment; hydrothermal stirring the solid sample, followed by filtration to recover a residue, and drying the residue to obtain a mixed sample of Co3O4, TiO2, and biochar, labeled as TCO; ultrasonically dispersing the attapulgite in an acid solution, stirring in a water bath at 80° C.

Abstract: An emulsion composition, a polystyrene nano-fiber, a polystyrene nano-fiber product and a preparation method and use thereof, wherein the emulsion composition comprises a dispersed phase and a continuous phase, the dispersed phase contains a soluble salt and a first solvent, the continuous phase contains polystyrene, a second solvent and sulfonated polystyrene being syndiotactic polystyrene and/or isotatic polystyrene; the preparation of the emulsion composition: under heating and stirring, dropwise adding the dispersed phase into the continuous phase; the preparation of the polystyrene nano-fiber or polystyrene nano-fiber product: crystallize the above emulsion composition; the polystyrene nano-fiber prepared by the above emulsion composition has a pore structure, and the prepared product has a stable and controllable three-dimensional structure and multi-level and/or intercommunicated pore structure, and also has a high preparation efficiency, therefore the above polystyrene nano-fiber or product has excell

Abstract: The present disclosure provides a honeycomb catalyst for catalytic oxidative degradation of VOCs prepared by an ultrasonic double-atomization process.

Abstract: The present disclosure provides a honeycomb catalyst for catalytic oxidative degradation of VOCs prepared by an ultrasonic double-atomization process.

Abstract: An emulsion composition, a polystyrene nano-fiber, a polystyrene nano-fiber product and a preparation method and use thereof, wherein the emulsion composition comprises a dispersed phase and a continuous phase, the dispersed phase contains a soluble salt and a first solvent, the continuous phase contains polystyrene, a second solvent and sulfonated polystyrene being syndiotactic polystyrene and/or isotatic polystyrene; the preparation of the emulsion composition: under heating and stirring, dropwise adding the dispersed phase into the continuous phase; the preparation of the polystyrene nano-fiber or polystyrene nano-fiber product: crystallize the above emulsion composition; the polystyrene nano-fiber prepared by the above emulsion composition has a pore structure, and the prepared product has a stable and controllable three-dimensional structure and multi-level and/or intercommunicated pore structure, and also has a high preparation efficiency, therefore the above polystyrene nano-fiber or product has excell