Abstract: Described herein is an aging process of a solution-heat-treated and quenched 2XXX-series aluminum alloy wrought product, comprising the steps of: (1) aging the product in a first aging step at one or more temperatures within a range of 90° C. to 120° C. for a cumulative period of time of at least 10 hours; and (2) subsequently aging the product in a second aging step at one or more temperatures within a range of 150° C. to 205° C. for a cumulative period of time of at least 4 hours. The wrought aluminum alloy can be processed to various product forms, e.g., sheet, thin plate, thick plate, extruded or forged products.

Abstract: A method of producing an integrated monolithic aluminum structure, comprising: providing an aluminum alloy plate with a thickness of at least 38.1 mm, wherein the plate is a 2xxx-series alloy in a T3-temper and has a composition comprising, in wt. %: Cu 3.8-4.5, Mn 0.3-0.8, Mg 1.1-1.6, Si up to 0.15, Fe up to 0.20, Cr up to 0.10, Zn up to 0.25, Ti up to 0.15, Ag up to 0.10, balance aluminum; optionally pre-machining the plate to an intermediate machined structure; high-energy hydroforming the plate or intermediate structure against a rigid die forming surface having a desired curvature contour of the integrated monolithic aluminum structure, causing the plate or the intermediate structure to conform to the forming surface contour; machining or mechanical milling the high-energy formed structure to a near-final or final machined integrated monolithic aluminum structure; ageing the final integrated monolithic aluminum structure to a desired temper.

Abstract: A method of manufacturing an AA2xxx-series aluminium alloy plate product having improved fatigue failure resistance and a reduced number of flaws, the method comprising the following steps (a) casting an ingot of an aluminium alloy of the 2xxx-series, the aluminium alloy comprising (in wt. %): Cu 1.9 to 7.0, Mg 0.3 to 1.8, Mn up to 1.2, balance aluminium and impurities, each 0.05 max., total 0.15; (b) homogenizing and/or preheating the cast ingot; (c) hot rolling the ingot into a plate product by rolling the ingot with multiple rolling passes characterized in that, when at an intermediate thickness of the plate between 100 and 200 mm, at least one high reduction hot rolling pass is carried out with a thickness reduction of at least 15%; wherein the plate product has a final thickness of less than 60 mm. The invention is also related to an aluminium alloy product produced by this method.

Abstract: A method of producing an integrated monolithic aluminum structure, the method including the steps of: (a) providing an aluminum alloy plate with a predetermined thickness of at least 25.4 mm, wherein the aluminum alloy plate is a 7xxx-series alloy provided in a W-temper; (b) optionally pre-machining of the aluminum alloy plate to an intermediate machined structure; (c) high-energy hydroforming of the plate or optional intermediate machined structure against a forming surface of a rigid die having a contour in accordance with a desired curvature of the integrated monolithic aluminum structure, the high energy hydroforming causing the plate or the intermediate machined structure to conform to the contour of the forming surface to at least one of a uniaxial curvature and a biaxial curvature; (d) solution heat-treating and cooling of the high-energy hydroformed structure; (e) machining and (f) ageing of the final integrated monolithic aluminum structure.

Abstract: A method of producing an integrated monolithic aluminum structure including providing an 7xxx-series aluminum alloy plate with a predetermined thickness of at least 10 mm, and wherein the plate has been solution heat treated and stretched, heat-treating the plate product in a first of a plurality of artificial ageing steps required to achieve a final temper state, high-energy hydroforming the plate against a forming surface of a rigid die having a contour with a desired curvature of the integrated monolithic aluminum structure, the high energy forming causing the aluminum alloy plate to conform to the forming surface contour to at least one of a uniaxial curvature and a biaxial curvature, heat-treating the integrated monolithic aluminum structure through a remaining ageing step of the ageing steps to achieve a desired final temper, and machining the high-energy formed structure to a near-final or final machined integrated monolithic aluminum structure.

Abstract: A method of manufacturing a rolled wear-resistant aluminium alloy product including the steps of: (a) providing a rolling feedstock material of an aluminium alloy having Mg 4.20% to 5.5%, Mn 0.50% to 1.1%, Fe up to 0.40%, Si up to 0.30%, Cu up to 0.20%, Cr up to 0.25%, Zr up to 0.25%, Zn up to 0.30%, Ti up to 0.25%, unavoidable impurities and balance aluminium; (b) heating the rolling feedstock; (c) hot-rolling of the feedstock to an intermediate gauge in a range of 15 mm to 40 mm; (d) hot-rolling of the feedstock from intermediate gauge to a final gauge in a range of 3 mm to 15 mm and wherein the hot-mill exit temperature is in a range of 130-285° C.; (e) cooling of the hot-rolled feedstock to ambient temperature.

Abstract: A method of producing an integrated monolithic aluminum structure, the method includes the steps of: (a) providing an aluminum alloy plate with a predetermined thickness of at least 38.1 mm, wherein the aluminum alloy plate is a 7xxx-series alloy provided in an F-temper or an O-temper; (b) optionally pre-machining of the aluminum alloy plate to an intermediate machined structure; (c) high-energy hydroforming of the plate or optional intermediate machined structure against a forming surface of a rigid die having a contour in accordance with a desired curvature of the integrated monolithic aluminum structure, the high-energy hydroforming causing the plate or the intermediate machined structure to conform to the contour of the forming surface to at least one of a uniaxial curvature and a biaxial curvature; (d) solution heat-treating and cooling of the high-energy hydroformed structure; (e) machining and (f) ageing of the final integrated monolithic aluminum structure.

Abstract: A method of producing an integrated monolithic aluminum structure, the method including the steps of: (a) providing an aluminum alloy plate with a predetermined thickness of at least 3 mm, wherein the aluminum alloy plate is a 2xxx-series alloy provided in an F-temper or an O-temper; (b) optionally pre-machining of the aluminum alloy plate to an intermediate machined structure; (c) high-energy hydroforming of the plate or optional intermediate machined structure against a forming surface of a rigid die having a contour in accordance with a desired curvature of the integrated monolithic aluminum structure, the high-energy hydroforming causing the plate or the intermediate machined structure to conform to the contour of the forming surface to at least one of a uniaxial curvature and a biaxial curvature; (d) solution heat-treating and cooling of the high-energy hydroformed structure; (e) machining and (f) ageing of the final integrated monolithic aluminum structure.

Abstract: A method of manufacturing a rolled wear-resistant aluminium alloy product including the steps of: (a) providing a rolling feedstock material of an aluminium alloy having Mg 4.20% to 5.5%, Mn 0.50% to 1.1%, Fe up to 0.40%, Si up to 0.30%, Cu up to 0.20%, Cr up to 0.25%, Zr up to 0.25%, Zn up to 0.30%, Ti up to 0.25%, unavoidable impurities and balance aluminium; (b) heating the rolling feedstock; (c) hot-rolling of the feedstock to an intermediate gauge in a range of 15 mm to 40 mm; (d) hot-rolling of the feedstock from intermediate gauge to a final gauge in a range of 3 mm to 15 mm and wherein the hot-mill exit temperature is in a range of 130-285° C.; (e) cooling of the hot-rolled feedstock to ambient temperature.

Abstract: The invention relates to an accelerator used for setting and hardening and a method for accelerating and hardening hydraulic binding agents using said accelerator. The principal components of said accelerator are nitrates, aminoalcohols, hydroxycarboxylic acids and polyalcohols. The hardening acceleration is not connected with a rapid loss in processability, which is common in other accelerated systems.

Abstract: The invention relates to an accelerator used for setting and hardening and a method for accelerating and hardening hydraulic binding agents using said accelerator. The principal components of said accelerator are nitrates, aminoalcohols, hydroxycarboxylic acids and polyalcohols. The hardening acceleration is not connected with a rapid loss in processability, which is common in other accelerated systems.