Abstract: A process for manufacturing powder metallurgy (P/M) preforms which are conditioned for optimum intrinsic workability is described which comprises steps of heating a quantity of P/M material in a can to a first preselected temperature under vacuum to degas the material, compacting the canned material at a second preselected temperature under pressure to provide a compact of the material; or cold compacting the powder to about 75% density and degassing it at suitable temperature and then vacuum hot pressing the powder at about 0.

Abstract: The conductor contains high-purity aluminum embedded in an aluminum-iron-cerium alloy matrix. It is not superconducting but still has extremely low electrical resistance at service temperatures. Selection of the aluminum-base alloy matrix with diffusionless alloying elements (iron and cerium) allows production of a multifilamentary conductor with the aluminum filaments maintaining their original high purity and consequently their very low electrical resistivity, even after a high temperature annealing cycle is applied. The composite conductor has good properties for both electromagnetic and thermal diffusion, which are critical to high-power, fast-pulse operation.

Abstract: An improved hot forming method for metals, alloys and the like, and in particular, for difficult to process high strength and high temperature metals and alloys of particular use in aerospace applications, is described, which comprises the steps of generating flow stress data as a function of strain rate and temperature on samples of the material at predetermined strain within predetermined ranges of temperature and strain rate; determining from that data the strain rate sensitivity and power dissipation efficiency of the material within the ranges of temperature and strain rate represented by the generated data; selecting values of strain rate and corresponding temperature for a selected value of the dissipation efficiency for the material; and hot forming the material at the selected strain rate and temperature values to a predetermined shape.

Abstract: Polycrystalline titanium-based alloys having a high specific strength are formed by the rapid solidification of a melt composition containing about 80 weight percent titanium and specific amounts of aluminum, vanadium, iron and copper. In the form of filaments the alloys are particularly useful as reinforcing agents in composite structures while in the form of powders the alloys are eminently suitable for use in the fabrication of structural components by the application of powder metallurgy technology.