Abstract: The manufacturing method includes a mixing step of mixing a plurality of zeolite particles, an inorganic binding material and an organic binder, to prepare a zeolite raw material; a forming step of extruding the zeolite raw material to obtain a formed zeolite article; and a firing step of firing the formed zeolite article to prepare the zeolite structure, the mixing step uses the inorganic binding material containing at least one type of silica sol selected from the group consisting of acid silica sol, silica sol containing silica particles coated with alumina, cationic silica sol, silica sol containing string-like silica particles, and silica sol containing bead-like silica particles, and a content ratio of silica particles contained in the silica sol selected from the group is from 10 to 30 mass % with respect to 100 mass % of the zeolite particles.

Abstract: The zeolite structure includes a zeolite material containing a plurality of zeolite particles and an inorganic binding material which binds the zeolite particles to one another, the plurality of zeolite particles include fine zeolite particles having a small average particle diameter and coarse zeolite particles which have an average particle diameter of three or more times the average particle diameter of the fine zeolite particles and which are not an agglomerated material of primary particles, a ratio of volumes of the coarse zeolite particles with respect to the whole volume of the plurality of zeolite particles is from 40 to 90 vol %, in the zeolite material, a ratio of a volume of the inorganic binding material is from 5 to 50 vol %, and a zeolite raw material containing the plurality of zeolite particles and the inorganic binding material is extruded to form a zeolite structure.

Abstract: A formed zeolite honeycomb article comprises a formed article obtained by extruding a zeolite raw material containing zeolite particles, an inorganic binding material and a filler constituted of plate-like particles in a honeycomb shape including partition walls disposed to form a plurality of cells, a drying shrinkage of the partition walls in a thickness direction thereof is larger than a drying shrinkage of the partition walls in a cell extending direction thereof and a drying shrinkage of the partition walls in a diametric direction perpendicular to the cell extending direction thereof, and the drying shrinkage of the partition walls in the thickness direction thereof is 1.2 or more times the drying shrinkage of the partition walls in the diametric direction perpendicular to the cell extending direction thereof in the formed zeolite honeycomb article.

Abstract: The zeolite structure is a porous zeolite structure constituted of a formed article obtained by extruding a zeolite raw material containing zeolite particles and an inorganic binding material including at least basic aluminum chloride, a ratio P1 (P1=V2/V1×100) of a volume V2 of the inorganic binding material in the zeolite structure with respect to a volume V1 of the zeolite structure is from 10 to 50 vol %, and a relation of equation (1) is satisfied: P2/P1?1.0 ??(1), in which P1 is the ratio of the volume V2 of the inorganic binding material in the zeolite structure with respect to the volume V1 of the zeolite structure and P2 (P2=Vb/Va×100) is a ratio of volumes Vb of pores having pore diameters of 0.003 to 0.03 ?m with respect to the whole pore volume Va of the zeolite structure.