Abstract: A foam molded body has a cylindrical shape, is produced by foaming a resin, and has a mass per unit area of 0.090 g/cm2 or less and an expansion ratio of from 3.4 to 40 times. A duct for an air conditioner and a duct for a vehicle air conditioner include a foam molded body that has a cylindrical shape, is produced by foaming a resin, and has a mass per unit area of 0.090 g/cm2 and an expansion ratio of from 3.4 to 40 times.

Abstract: A foam molded body has a cylindrical shape, is produced by foaming a resin, and has a mass per unit area of 0.090 g/cm2 or less and an expansion ratio of from 3.4 to 40 times. A duct for an air conditioner and a duct for a vehicle air conditioner include a foam molded body that has a cylindrical shape, is produced by foaming a resin, and has a mass per unit area of 0.090 g/cm2 and an expansion ratio of from 3.4 to 40 times.

Abstract: The present invention relates to a resin composition for a nano concave-convex structure, including 0.01 to 10 parts by mass of an active energy ray polymerization initiator (D), 0.01 to 3 parts by mass of a release agent (E), and 0.01 to 3 parts by mass of a lubricant (F), relative to 100 parts by mass of a polymerization reactive monomer component containing 50 to 95 parts by mass of a tetrafunctional (meth)acrylate monomer (A), 5 to 35 parts by mass of a difunctional (meth)acrylate monomer (B) in which the total number of repeating units within a polyalkylene glycol structure is from 4 to 25, and not more than 15 parts by mass of a monofunctional (meth)acrylate monomer (C) which is copolymerizable with the monomers (A) and (B), and relates to a transparent member for the monitor of a vehicle navigation device and the cover of a vehicle meter.

Abstract: A display apparatus includes: a liquid crystal panel (31); a touch panel (31) placed on the liquid crystal panel (31); a base material layer (37, 40) stacked on the touch panel (34); and an adhesive layer (36, 39) interposed between the touch panel (34) and the base material layer (37, 40). Fiber having properties to solve polarization is contained in at least one of the base material layer (37, 40) and the adhesive layer (36, 39).

Abstract: A display apparatus includes: a liquid crystal panel (31); a touch panel (31) placed on the liquid crystal panel (31); a base material layer (37, 40) stacked on the touch panel (34); and an adhesive layer (36, 39) interposed between the touch panel (34) and the base material layer (37, 40). Fiber having properties to solve polarization is contained in at least one of the base material layer (37, 40) and the adhesive layer (36, 39).

Abstract: The present invention relates to a resin composition for a nano concave-convex structure, including 0.01 to 10 parts by mass of an active energy ray polymerization initiator (D), 0.01 to 3 parts by mass of a release agent (E), and 0.01 to 3 parts by mass of a lubricant (F), relative to 100 parts by mass of a polymerization reactive monomer component containing 50 to 95 parts by mass of a tetrafunctional (meth)acrylate monomer (A), 5 to 35 parts by mass of a difunctional (meth)acrylate monomer (B) in which the total number of repeating units within a polyalkylene glycol structure is from 4 to 25, and not more than 15 parts by mass of a monofunctional (meth)acrylate monomer (C) which is copolymerizable with the monomers (A) and (B), and relates to a transparent member for the monitor of a vehicle navigation device and the cover of a vehicle meter.

Abstract: There is provided a polycarbonate resin composition containing aluminum oxide nanoparticles and being capable of showing good moldability and retention heat stability and combining high transparency and dimensional stability with excellent mechanical properties. The polycarbonate resin composition is characterized by containing an organic acid and aluminum oxide and in that: the resin composition has a melt mass flow rate of 11 g/10 min or higher as measured according to JIS K 7210 under the conditions of a temperature of 280° C., a nominal load of 2.16 Kg and a nozzle dimension L/D of 8/2; and a No. 2 dumbbell-shaped specimen according to JIS K 7113 formed by heat-press molding the resin composition into a film of 0.2 mm in thickness and cutting the film has a breaking stress of 8 MPa or higher as measured under the conditions of a temperature of 23° C., a humidity of 50% RH and a tensile rate of 50 mm/min.

Abstract: There is provided a polycarbonate resin composition containing aluminum oxide nanoparticles and being capable of showing good moldability and retention heat stability and combining high transparency and dimensional stability with excellent mechanical properties. The polycarbonate resin composition is characterized by containing an organic acid and aluminum oxide and in that: the resin composition has a melt mass flow rate of 11 g/10 min or higher as measured according to JIS K 7210 under the conditions of a temperature of 280° C., a nominal load of 2.16 Kg and a nozzle dimension UD of 8/2; and a No.2 dumbbell-shaped specimen according to JIS K 7113 formed by heat-press molding the resin composition into a film of 0.2 mm in thickness and cutting the film has a breaking stress of 8 MPa or higher as measured under the conditions of a temperature of 23° C., a humidity of 50% RH and a tensile rate of 50 min/min.

Abstract: Surface-coated aluminum oxide nanoparticles capable of being uniformly blended into polycarbonate resin in a good dispersed state while maintaining a molecular weight of the polycarbonate resin at a specific level or more. Surfaces of the surface-coated aluminum oxide nanoparticles are coated with a dispersant and a silylation reagent. In a case where a monochromated Al-K? ray is irradiated onto a sample surface by using an X-ray photoelectron spectroscope, when a surface element composition is calculated from an obtained photoelectron peak area, contents (atm %) of nitrogen atoms, thiol-derived sulfur atoms, and halogen atoms in the surface-coated aluminum oxide nanoparticles are individually 2 or less, and when the surface element composition is calculated from obtained photoelectron peak areas of Al2p and Si2s, a concentration (mol %) of silicon atoms with respect to aluminum atoms is 0.05 to 30.

Abstract: A resin composition of the present invention has resin and a metal oxide particle composite contained in the resin as filler. The metal oxide particle composite has a metal oxide particle and an organic phosphorus compound chemically bonded to a surface of the metal oxide particle. The resin composition includes high aspect ratio metal oxide particles uniformly dispersed and is excellent in both the mechanical properties and transparency.