Patents by Inventor Hassan Moenes El Dekki
Hassan Moenes El Dekki has filed for patents to protect the following inventions. This listing includes patent applications that are pending as well as patents that have already been granted by the United States Patent and Trademark Office (USPTO).
-
Patent number: 8734750Abstract: Sodium silicate solutions of modulus 3.0 to 3.8 are provided. In some embodiments, the solution is made by a process that uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: GrantFiled: June 28, 2013Date of Patent: May 27, 2014Assignee: The National Titanium Dioxide Co. Ltd. (CRISTAL)Inventors: Fadi Mohammed Saeed Trabzuni, Hassan Moenes El Dekki, Chathangat Cheroolil Gopalkrishnan
-
Publication number: 20130284974Abstract: Sodium silicate solutions of modulus 3.0 to 3.8 are provided. In some embodiments, the solution is made by a process that uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: ApplicationFiled: June 28, 2013Publication date: October 31, 2013Inventors: Fadi Mohammed Saeed TRABZUNI, Hassan Moenes EL DEKKI, Chathangat Cheroolil GOPALKRISHNAN
-
Patent number: 8512664Abstract: A method is provided for treating silica sand scrubs (SSS) generated and accumulated as waste in the chloride manufacturing process of titanium dioxide pigment. A hydrothermal process is used to produce sodium silicate solutions of modulus 3.0 to 3.8, and precipitated silicas. In some embodiments, the process uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: GrantFiled: October 16, 2012Date of Patent: August 20, 2013Assignee: The National Titanium Dioxide Co. Ltd. (CRISTAL)Inventors: Fadi Mohammed Saeed Trabzuni, Hassan Moenes El Dekki, Chathangat Cheroolil Gopalkrishnan
-
Patent number: 8287833Abstract: A method is provided for treating silica sand scrubs (SSS) generated and accumulated as waste in the chloride manufacturing process of titanium dioxide pigment. A hydrothermal process is used to produce sodium silicate solutions of modulus 3.0 to 3.8, and precipitated silicas. In some embodiments, the process uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: GrantFiled: September 21, 2011Date of Patent: October 16, 2012Assignee: The National Titanium Dioxide Co. Ltd. (CRISTAL)Inventors: Fadi Mohammed Saeed Trabzuni, Hassan Moenes El Dekki, Chathangat Cheroolil Gopalkrishnan
-
Publication number: 20120007023Abstract: A method is provided for treating silica sand scrubs (SSS) generated and accumulated as waste in the chloride manufacturing process of titanium dioxide pigment. A hydrothermal process is used to produce sodium silicate solutions of modulus 3.0 to 3.8, and precipitated silicas. In some embodiments, the process uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: ApplicationFiled: September 21, 2011Publication date: January 12, 2012Applicant: THE NATIONAL TITANIUM DIOXIDE CO. LTD. (CRISTAL)Inventors: Fadi Mohammed Saeed TRABZUNI, Hassan Moenes EL DEKKI, Chathangat Cheroolil GOPALKRISHNAN
-
Patent number: 8057770Abstract: A method is provided for treating silica sand scrubs (SSS) generated and accumulated as waste in the chloride manufacturing process of titanium dioxide pigment. A hydrothermal process is used to produce sodium silicate solutions of modulus 3.0 to 3.8, and precipitated silicas. In some embodiments, the process uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: GrantFiled: October 28, 2009Date of Patent: November 15, 2011Assignee: The National Titanium Dioxide Co., Ltd. (CRISTAL)Inventors: Fadi Mohammed Saeed Trabzuni, Hassan Moenes El Dekki, Chathangat Cheroolil Gopalkrishnan
-
Publication number: 20100044629Abstract: A method is provided for treating silica sand scrubs (SSS) generated and accumulated as waste in the chloride manufacturing process of titanium dioxide pigment. A hydrothermal process is used to produce sodium silicate solutions of modulus 3.0 to 3.8, and precipitated silicas. In some embodiments, the process uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: ApplicationFiled: October 28, 2009Publication date: February 25, 2010Applicant: The Titanium Dioxide Co., Ltd. (CRISTAL)Inventors: Fadi Mohammed Saeed Trabzuni, Hassan Moenes El Dekki, Chathangat Cheroolil Gopalkrishnan
-
Patent number: 7622097Abstract: A method is provided for treating silica sand scrubs (SSS) generated and accumulated as waste in the chloride manufacturing process of titanium dioxide pigment. A hydrothermal process is used to produce sodium silicate solutions of modulus 3.0 to 3.8, and precipitated silicas. In some embodiments, the process uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: GrantFiled: July 20, 2007Date of Patent: November 24, 2009Assignee: The National Titanium Bioxide Co., Ltd. (CRISTAL)Inventors: Fadi Mohammed Saeed Trabzuni, Hassan Moenes El Dekki, Chathangat Cheroolil Gopalkrishnan
-
Publication number: 20090022646Abstract: A method is provided for treating silica sand scrubs (SSS) generated and accumulated as waste in the chloride manufacturing process of titanium dioxide pigment. A hydrothermal process is used to produce sodium silicate solutions of modulus 3.0 to 3.8, and precipitated silicas. In some embodiments, the process uses two specific principal reaction stages. A sodium silicate solution having a low SiO2:Na2O molar ratio, in the range from 2.0 to 2.8, is first produced by reaction of the SSS, as a cost-effective SiO2 source, with aqueous caustic soda. The conversion of this intermediate sodium silicate solution of low modulus to a high SiO2:Na2O molar ratio is made possible by using a SiO2 source that is prepared as precipitated amorphous silica from the intermediate sodium silicate solution produced above.Type: ApplicationFiled: July 20, 2007Publication date: January 22, 2009Applicant: The Titanium Dioxide Co. Ltd. (CRISTAL)Inventors: Fadi Mohammed Saeed Trabzuni, Hassan Moenes El Dekki, Chathangat Cheroolil Gopalkrishnan