Abstract: A silver base electrical contact material is described which contains uniformly in a silver matrix dispersed particles of nickel, nickel oxide, and at least one additive selected from the group consisting of vanadium, manganese, chromium, thallium, titanium, cobalt, and tungsten carbide. The contact material contains 1.3 to 24.8 wt % of nickel, 0.2 to 4.7 wt % of nickel oxide, 0.05 to 3 wt % of the additive, and balance silver. A superior silver base contact material having excellent welding and wear resistances is obtained by adding the metals and the metal carbide to a silver-nickel-nickel oxide contact material.

Abstract: A silver base electrical contact material with superior resistance to arc erosion along with improved wear and welding resistance. The contact material consists essentially of 0.5 to 39.9 wt % of nickel, 0.14 to 7.0 wt % of nickel oxides, and balance silver. The material contains not less than 0.4 wt % of nickel responsible for constituting minute nickel and nickel particles which have a particle size of not more than 1 .mu.m and are dispersed in a silver matrix for strengthening the material to give improved wear and welding resistance. The dispersed minute nickel oxide particles are included to stabilize arcing occurring at the time of opening and closing contacts in such a manner as to anchor one end of an arc substantially at any immediately available point over the entire contact surface as soon as the arcing occurs, thereby preventing the arc end from moving violently across or beyond the contact surface and therefore minimizing arc related damages or arc erosion.

Abstract: A silver base electrical contact material with superior resistance to arc erosion along with improved wear and welding resistance. The contact material consists essentially of 0.5 to 39.9 wt % of nickel, 0.14 to 7.0 wt % of nickel oxides, and balance silver. The material contains not less than, 0.4 wt % of nickel responsible for constituting minute nickel and nickel particles which have a particle size of not more than 1 .mu.m and are dispersed in a silver matrix for strengthening the material to give improved wear and welding resistance. The dispersed minute nickel oxide particles are included to stabilize arcing occurring at the time of opening and closing contacts in such a manner as to anchor one end of an arc substantially at any immediately available point over the entire contact surface as soon as the arcing occurs, thereby preventing the arc end from moving violently across or beyond the contact surface and therefore minimizing arc related damages or arc erosion.