Abstract: A sinterable and/or fusible ceramic mass is disclosed, having a long-term stable compound of crystalline phases of apatite, wollastonite, titanite and optionally cristobalite, which is stabilized by a glass phase, and a production process therefor. The ceramic mass can be obtained by sintering a mixture comprising at least the constituents SiO2, CaO, P2O5, MgO, CaF2 and TiO2, on their own or in combination with at least one alkali oxide, the alkali oxide being chosen from NaO2 and K2O. The invention further relates to uses of the sintered material in the form of shaped articles for strengthening, cleaning, roughening or polishing surfaces of medical implants or as a final prosthesis.

Abstract: A sinterable and/or fusible ceramic mass is disclosed, having a long-term stable compound of crystalline phases of apatite, wollastonite, titanite and optionally cristobalite, which is stabilized by a glass phase, and a production process therefor. The ceramic mass can be obtained by sintering a mixture comprising at least the constituents SiO2, CaO, P2O5, MgO, CaF2 and TiO2, on their own or in combination with at least one alkali oxide, the alkali oxide being chosen from NaO2 and K2O. The invention further relates to uses of the sintered material in the form of shaped articles for strengthening, cleaning, roughening or polishing surfaces of medical implants or as a final prosthesis.

Abstract: The present invention relates to a powder mixture for resorbable calcium phosphate biocements, which mixture consists of 40–99% by volume of powder having a particle size of 0.1–10 ?m, 1–20% by volume of powder having a particle size of 10–43 ?m and 0–59% by volume of powder having a particle size of 43–315 ?m, which powder is obtained by grinding the spontaneously crystallizing melts of a material comprising crystalline and X-ray amorphous phases, which material a) according to 31P-NMR measurements, contains Q0-groups of orthophosphate and Q1-groups of diphosphate, the orthophosphates or Q0-groups making up 65 to 99.9% by weight relative to the total phosphorus content of the powder mixture and the diphosphates or Q1-groups making up 0.1 to 35% by weight relative to the total phosphorus content of the powder mixture, and b) according to X-ray diffractometric measurements and relative to the total weight of the powder mixture, contains 35 to 99.

Abstract: The present invention relates to a powder mixture for resorbable calcium phosphate biocements, which mixture consists of 40-99% by volume of powder having a particle size of 0.