Abstract: The disclosure relates to a granular, refractory mineral elasticizing granulate for refractory products, in particular for basic refractory products. The minerals consist of mono-phased sintered spinel mixed crystal of the ternary system MgO—Fe2O3—Al2O3 of the composition range MgO: 12 to 19.5, in particular 15 to 17 wt.-%, Remainder: Fe2O3 and Al2O3 in a quantity ratio range of Fe2O3 to Al2O3 between 80 to 20 and 40 to 60 wt.-%. Starting from an MgO content between 12 and 19.5 wt.-%, the respective mixed crystals have an Fe2O3 and Al2O3 content in a solid solution out of the limited ranges respectively indicated thereof, such that a total composition of 100% is obtained. In addition, the invention relates to a method for production of the elasticizing granulate and to the use thereof.

Abstract: The invention relates to a granular, refractory mineral elasticizing granulate for refractory products, in particular for basic refractory products. The minerals consist of mono-phased fused spinel mixed crystal or multi-phased fusion products of the ternary system MgO?Fe2O3—Al2O3 of the composition range MgO: 12 to 19.5, in particular 15 to 17 wt.- %, Remainder: Fe2O3 and Al2O3 in a quantity ratio range of Fe2O3 to Al2O3 between 80 to 20 and 40 to 60 wt.- %. Starting from an MgO content between 12 and 19.5 wt.- %, the respective mixed crystals have an Fe2O3 and Al2O3 content in a solid solution out of the limited ranges respectively indicated thereof, such that a total composition of 100% is obtained. In addition, the invention relates to a method for production of the elasticizing granulate and to the use thereof.

Abstract: The invention relates to a refractory batch and to a process for its production. The batch comprises a refractory metal oxide main component containing Al2O3; the refractory metal oxide main component containing 40 to 60% by weight of Al2O3; a phosphate bond, in particular, the phosphate bond being produced by at least one of a phosphoric acid and a monoaluminum phosphate; finely particulate SiC having a grain size of <0.2 mm, the batch containing 3 to 15% by weight of the finely particulate SiC; and the grain size distribution of the SiC being selected so that more than 2.0% of the SiC, based on a total quantity of the batch, is <0.045 mm, whereby said batch excludes the presence of boron phosphate.

Abstract: The invention relates to a refractory batch and to a process for its production. The batch comprises a refractory metal oxide main component containing Al2O3; the refractory metal oxide main component containing 40 to 60% by weight of Al2O3; a phosphate bond, in particular, the phosphate bond being produced by at least one of a phosphoric acid and a monoaluminum phosphate; finely particulate SiC having a grain size of <0.2 mm, the batch containing 3 to 15% by weight of the finely particulate SiC; and the grain size distribution of the SiC being selected so that more than 2.0% of the SiC, based on a total quantity of the batch, is <0.045 mm, whereby said batch excludes the presence of boron phosphate.

Abstract: The invention relates to a refractory batch and to a process for its production. The batch comprises a refractory metal oxide main component containing Al2O3; the refractory metal oxide main component containing 40 to 60% by weight of Al2O3; a phosphate bond, in particular, the phosphate bond being produced by at least one of a phosphoric acid and a monoaluminum phosphate; finely particulate SiC having a grain size of <0.2 mm, the batch containing 3 to 15% by weight of the finely particulate SiC; and the grain size distribution of the SiC being selected so that more than 2.0% of the SiC, based on a total quantity of the batch, is <0.045 mm, whereby said batch excludes the presence of boron phosphate.

Abstract: A batch, in particular for the production of refractory shaped bodies, includes a mixture of a refractory, metal oxide main component containing 40 to 60% by weight of Al2O3, a phosphate bond and finely particulate SiC having a grain size of <0.2 mm, and a process using the mixture for forming the batch to produce the refractory shaped bodies.

Abstract: The invention relates to a batch, in particular for the production of refractory shaped bodies, which includes a refractory, metal oxide main component containing 40 to 60% by weight of Al2O3, a phosphate bond and finely particulate SiC with a grain size of <0.2 mm, and to a process for its production.