Abstract: The present disclosure relates to an inorganic, halogen-free flameproofing agent made of modified, rehydrated red mud (MR2S), having a mineral composition of 10 to 50 weight percent of iron compounds, 12 to 35 weight percent of aluminum compounds, 5 to 17 weight percent of silicon compounds, 2 to 21 weight percent of TiO2, and 0.5 to 6 weight percent of calcium compounds, wherein the compounds of iron have a hydroxide and oxide hydrate fraction greater than or equal to 50 weight percent relative to the oxide fraction of the iron compounds, and wherein the compounds of aluminum have a hydroxide and oxide hydrate fraction greater than or equal to 50 weight percent. The disclosure further relates to a flameproofed material system comprising a flammable material and the inorganic, halogen-free flameproofing agent and to a method for the production thereof.

Abstract: The invention relates to an inorganic, halogen-free flameproofing agent made of modified, rehydrated red mud (MR2S), having a mineral composition of 10 to 50 weight percent of iron compounds, 12 to 35 weight percent of aluminum compounds, 5 to 17 weight percent of silicon compounds, 2 to 21 weight percent of TiO2, and 0.5 to 6 weight percent of calcium compounds, wherein the compounds of iron have a hydroxide and oxide hydrate fraction greater than or equal to 50 weight percent, preferably greater than or equal to 80 weight percent, relative to the oxide fraction of the iron compounds, and wherein the compounds of aluminum have a hydroxide and oxide hydrate fraction greater than or equal to 50 weight percent, preferably greater than or equal to 80 weight percent, relative to the oxide fraction of the aluminum compounds. The invention further relates to a flameproofed material system comprising a flammable material and the inorganic, halogen-free flameproofing agent and to a method for the production thereof.

Abstract: In the manufacture of viscose, and an elongate cellulose member such as standard viscose rayon fibre, with reduced alkali ratio from dissolving-grade cellulose such as wood pulp by irradiation with a high energy beam at a dose of 1-30 kGy, steeping in aqueous sodium hydroxide, pressing to form alkali cellulose, xanthating to form cellulose xanthate, dissolving in aqueous liquor to form viscose and (when elongate cellulose members are required) extruding through a die into an acid bath for coagulation and regeneration to form an elongate cellulose member which is then washed and dried, viscose filtration can be improved by including in the dissolving liquor for the cellulose xanthate an amount of from 200 to 10000 ppm by weight of a salt which consists of alkali metal or ammonium cations and anions of a strong acid.