Abstract: A method of conditioning the surface of a work piece, in particular of a litho-strip or litho-sheet, consisting of an aluminum alloy enables an increase in manufacturing speed in surface roughening while maintaining a high quality of the electro-chemical grained surface of the work piece with relative low effort related to facility equipment. The method of conditioning comprises at least the step of degreasing the surface of the work piece with a degreasing medium, wherein the degreasing medium contains at least 1.5 to 3% by weight of a composite of 5-40% sodium tripolyphosphate, 3-10% sodium gluconate, 3-8% of a composite of non-ionic and anionic surfactants and optionally 0.5 to 70% soda, wherein sodium hydroxide is added to the degreasing medium such that the concentration of sodium hydroxide in the aqueous degreasing medium is 0.01 to 5% by weight.

Abstract: A method of conditioning the surface of a work piece, particularly of a strip or sheet, more particularly of a lithostrip or lithosheet, including an aluminum alloy is provided. The method for conditioning the surface of a work piece and a work piece including an aluminum alloy enabling an increasing manufacturing speed in electro-chemically graining and maintaining at the same time a high quality of the grained surface, includes a conditioning method which comprises at least the two steps, degreasing the surface of the work piece with a degreasing medium and subsequently cleaning the surface of the work piece by pickling.

Abstract: The invention relates to a method for producing a strip made of an AlMgSi alloy in which a rolling ingot is cast of an AlMgSi alloy, the rolling ingot is subjected to homogenization, the rolling ingot which has been brought to rolling temperature is hot-rolled, and then is optionally cold-rolled to the final thickness thereof. The problem of providing a method for producing an aluminum strip made of an AlMgSi alloy and an aluminum strip, which has a higher breaking elongation with constant strength and therefore enables higher degrees of deformation in producing structured metal sheets, is solved in that the hot strip has a temperature of no more than 130° C. directly at the exit of the last rolling pass, preferably a temperature of no more than 100° C., and the hot strip is coiled at that or a lower temperature.

Abstract: An aluminum alloy for producing an aluminum strip for lithographic print plate carriers, a method for producing an aluminum alloy for lithographic print plate carriers, in which, during the production of the aluminum alloy, after the electrolysis of the aluminum oxide, the liquid aluminum, up to the casting of the aluminum alloy, is supplied to a plurality of purification steps, as well as an aluminum strip for lithographic print plate carriers and a corresponding use of the aluminum strip for lithographic print plate carriers include a carbide content of less than 10 ppm, and preferably less than 1 ppm. As a result, the aluminum alloy, the method for producing the aluminum alloy, the aluminum strip, and corresponding use of the aluminum strip for lithographic print plate carriers described herein allow for the use of virtually gas-tight coatings.

Abstract: A method of conditioning the surface of a work piece, particularly of a strip or sheet, more particularly of a lithostrip or lithosheet, including an aluminum alloy is provided. The method for conditioning the surface of a work piece and a work piece including an aluminum alloy enabling an increasing manufacturing speed in electro-chemically graining and maintaining at the same time a high quality of the grained surface, includes a conditioning method which comprises at least the two steps, degreasing the surface of the work piece with a degreasing medium and subsequently cleaning the surface of the work piece by pickling.

Abstract: The invention relates to an aluminium alloy for the production of lithographic printing plate supports and also to an aluminium strip produced from the aluminium alloy, a process for the production of the aluminium strip and also its use for the production of lithographic printing plate supports. The object of providing an aluminium alloy as well as an aluminium strip from an aluminium alloy that permits the production of printing plate supports having improved bending-strength fatigue transverse to the rolling direction without adversely affecting the tensile strength values before and after the annealing process and while preserving the roughening properties, is achieved by the fact that the aluminium alloy contains the following alloy components in weight per cent: 0.4%<Fe?1.0%, 0.3%<Mg?1.0%, 0.05%?Si?0.25%, Mn?0.25%, Cu?0.04%, Ti?0.1%, the remainder being Al and unavoidable impurities, individually at most 0.05% and totaling at most 0.05%.

Abstract: A method for producing aluminum strips for lithographic printing plate supports, wherein the aluminum strip is produced from a rolling ingot, which after optional homogenizing is hot-rolled to a thickness of 2 mm to 7 mm and cold-rolled to a final thickness of 0.15 mm to 0.5 mm provides for an aluminum strip having a thickness of 0.15 mm to 0.5 mm and a printing plate support produced from the aluminum strip.

Abstract: A strip for the production of a substrate for lithographic printing plates consisting of aluminum or an aluminum alloy and has at least to some extent a microcrystalline surface layer as a result of hot and/or cold roll passes. When analyzed in a two-dimensional microprobe analysis according to the mapping method of a surface region of the microcrystalline surface of the strip, the surface portion having an intensity ratio I/Ibulk(avg) of greater than 3 in the spectral range of the K?1 line of the X-ray emission spectrum of oxygen of the measured microcrystalline surface layer is less than 10%, preferably less than 7%, wherein, during the two-dimensional microprobe analysis, an excitation voltage of 15 kV, a beam current of 50 nA and a beam cross section of 1 ?m is used with a step size of 16.75 ?m for the electron beam.

Abstract: A method of conditioning the surface of a work piece, in particular of a litho-strip or litho-sheet, consisting of an aluminum alloy enables an increase in manufacturing speed in surface roughening while maintaining a high quality of the electro-chemical grained surface of the work piece with relative low effort related to facility equipment. The method of conditioning comprises at least the step of degreasing the surface of the work piece with a degreasing medium, wherein the degreasing medium contains at least 1.5 to 3% by weight of a composite of 5-40% sodium tripolyphosphate, 3-10% sodium gluconate, 3-8% of a composite of non-ionic and anionic surfactants and optionally 0.5 to 70% soda, wherein sodium hydroxide is added to the degreasing medium such that the concentration of sodium hydroxide in the aqueous degreasing medium is 0.01 to 5% by weight.

Abstract: An aluminum strip for lithographic printing plate supports, from which printing plate supports can be produced with an improved roughenability and at the same time improved mechanical properties, particularly after a burn-in process, is formed of an aluminum alloy which has the following proportions of alloy constituents in wt. %: 0.05%?Mg?0.3%, 0.008%?Mn?0.3%, 0.4%?Fe?1%, 0.05%?Si?0.5%, Cu?0.04%, Ti?0.04%, inevitable impurities individually max. 0.01%, in total max. 0.05% and remainder Al.

Abstract: A method of conditioning the surface of a work piece, particularly of a strip or sheet, more particularly of a lithostrip or lithosheet, including an aluminium alloy is provided. The method for conditioning the surface of a work piece and a work piece including an aluminium alloy enabling an increasing manufacturing speed in electro-chemically graining and maintaining at the same time a high quality of the grained surface, includes a conditioning method which comprises at least the two steps, degreasing the surface of the work piece with a degreasing medium and subsequently cleaning the surface of the work piece by pickling.