Abstract: A process for the production of a base foil of an aluminum alloy is provided which comprises a first heating step in which a cold-rolled plate derived from a continuously cast-rolled plate is maintained at a temperature between higher than 350° C. and lower than 450° C. for longer than 0.5 hour, the cast-rolled plate being comprised of a Al-Fe-Si type aluminum alloy, the aluminum alloy containing Fe in a content between more than 0.3% by weight and less than 1.2% by weight and Si in a content between more than 0.20% by weight and less than 1% by weight and having a Si/Fe ratio between above 0.4 and below 1.2, and a second heating step in which the resultant plate is maintained at a temperature between higher than 200° C. and lower than 330° C. for longer than 0.5 hour. The base foil is substantially free of macroscopic and microscopic rib patterns on its rolled and mat surfaces.