Abstract: The present invention provides ethylene-propylene-diene rubbers which are excellent in co-vulcanizability with conjugated diene rubbers and can impart excellent weather resistance, ozone resistance and thermal aging resistance without detriment to excellent mechanical characteristics, wear resistance and dynamic fatigue resistance which the conjugated diene rubbers possess.The ethylene-propylene-diene rubbers of the present invention are characterized by having a Mooney viscosity ML.sub.1+4 (100.degree. C.) of 50 to 120 and comprising(A) 90 to 40% by weight of a high-molecular weight ethylene-propylene-diene copolymer rubber having an ethylene content of 73 to 85 mol %, an intrinsic viscosity [.eta.] of 2.5 to 5.0 dl/g as measured at 135.degree. C. in decalin and an iodine value of 15 to 35, and(B) 10 to 60% by weight of a low-molecular-weight ethylene-propylene-diene copolymer rubber having an ethylene content of 73 to 85 mol %, an intrinsic viscosity [.eta.] of 0.15 to 0.8 dl/g as measured at 135.degree. C.

Abstract: A Langmuir-Blodgett ultrathin membrane is constituted of polyfumarate having a degree of polymerization of 20 to 10,000. The polyfumarate is obtained by polymerizing fumarate represented by the general formula of: ##STR1## wherein at least one of R.sub.1 and R.sub.2 represents a bulky hydrocarbon group such as a branched alkyl group, a cycloalkyl group or a substituent thereof, a fluorine-substituted hydrocarbon group, a hetero atom-containing hydrocarbon group or a silicon-containing group.

Abstract: Using the Langmuir-Blodgett's technique and a compound represented by the general formula CF.sub.3 (CF.sub.2).sub.n (CH.sub.2).sub.m --X, wherein X is a hydrophilic group, preferably --COOH, n is from 5 to 20 and m is from 0 to 10, a firm built-up film having a desired number of monomolecular layers can surely be formed on a solid substrate surface by spreading a monomolecular film of the fluorinated compound on an aqueous phase containing trivalent metal ions. In the obtained built-up film the CF.sub.3 -terminated molecules are well oriented in the direction of the thickness of the film. The built-up film fully exhibits extreme hydrophobicity, high insulation, low refraction and other properties characteristic of the fluorine-containing compound.