Abstract: A positive active material for a non-aqueous cell comprising a lithium-manganese composite oxide having an oxygen-defect type spinel structure and its preparing process are disclosed. A cell comprising the positive active material for a non-aqueous cell has excellent properties with high discharge capacity, a monotonous variation of the potential without flection during both charging and discharging, and very limited loss of the electric capacity upon charging and discharging.

Abstract: A nonaqueous polymer battery includes a lithium ion conductive polymer having pores, a positive active material, and a carbonaceous negative active material. In the nonaqueous polymer battery, the positive active material is represented by Li.sub.1-x CoO.sub.2 (0.ltoreq.x.ltoreq.1) wherein the molar ratio of the carbon atoms in the negative active material to the cobalt atoms in the positive active material is 7.5 or lower; the positive active material is represented by Li.sub.1-x NiO.sub.2 (0.ltoreq.x.ltoreq.1) wherein the molar ratio of the carbon atoms in the negative active material to the nickel atoms in the positive active material is less than 10; or the positive active material is represented by Li.sub.1-x Ni(Co)O.sub.2 (Li.sub.1-x NiO.sub.2 having not more than 20% of the nickel atoms thereof displaced with cobalt ions; 0.ltoreq.x.ltoreq.

Abstract: In a method for producing a lithium nickelate positive electrode, nickel hydroxide or nickel oxyhydroxide is held into an electrically conductive porous substrate to form an electrode plate, the electrode is treated with an alkaline solution containing lithium ion; and the electrode treated with the alkaline solution is heated at a temperature not higher than 450.degree. C.

Abstract: A positive electrode active material for lithium battery which is represented by general formula Li.sub.x Mn.sub.2-y M.sub.y O.sub.4 (M: a 2-valency metal selected from Ni, Co, Fe and Zn with 0.45.ltoreq.y.ltoreq.0.60, 1.ltoreq.x.ltoreq.2.1) having cubic spinel structure of lattice constant within 8.190 angstrom. Such an active material is manufactured by employing sol-gel process wherein one of inorganic salt, hydroxide and organic acid salt of lithium or a mixture of these for Li, one of inorganic salt and organic acid salt of manganese or a mixture of these for Mn, and one of inorganic salt and organic acid salt of the selected metal or a mixture of these for M are used as the starting materials for synthesis, ammonia water is added to the solutions of these starting materials in alcohol or water to obtain gelatinous material and the gelatinous material thus obtained is fired.

Abstract: A method for manufacturing positive a electrode active material for a lithium battery represented by general formula Li.sub.x Mn.sub.2-y M.sub.y O.sub.4 (M: a 2-valency metal, 0.45.ltoreq.y.ltoreq.0.60, 1.ltoreq.x.ltoreq.2.1) having cubic spinel structure of and a lattice constant within 8.190 angstroms by employing a solid phase reaction, comprising the steps of firing a lithium compound, a manganese compound and a metal M compound and refiring the fired material after pressurizing it at least once to remove a metal M oxide.

Abstract: A positive electrode active material for lithium battery which is represented by general formula Li.sub.x Mn.sub.2-y M.sub.y O.sub.4 (M: a 2-valency metal, 0.45.ltoreq.y.ltoreq.0.60, 1.ltoreq.x.ltoreq.2.1) having cubic spinel structure of lattice constant within 8.190 angstroms.

Abstract: In a method of producing a lithium nickelate according to the present invention, a cobalt containing oxy-nickel hydroxide of a .beta.-type, a .gamma.-type, or a mixture of a .beta.-type and a .gamma.-type is mixed with a lithium salt, and heat treatment is applied to the mixture at a temperature of 400.degree. C. to 500.degree. C.

Abstract: A positive electrode active material for lithium battery which is represented by general formula Li.sub.x Mn.sub.2-y M.sub.y O.sub.4 (M: a 2-valency metal selected from Ni, Co, Fe and Zn with 0.45.ltoreq.y.ltoreq.0.60, 1.ltoreq.x.ltoreq.2.1) having cubic spinel structure of lattice constant within 8.190 angstrom. Such an active material is manufactured by employing sol-gel process wherein one of inorganic salt, hydroxide and organic acid salt of lithium or a mixture of these for Li, one of inorganic salt and organic acid salt of manganese or a mixture of these for Mn, and one of inorganic salt and organic acid salt of the selected metal or a mixture of these for M are used as the starting materials for synthesis, ammonia water is added to the solutions of these starting materials in alcohol or water to obtain gelatinous material and the gelatinous material thus obtained is fired.

Abstract: A prismatic sealed alkaline storage battery with a nickel hydroxide electrode comprising a nickel substrate having a porosity of from 86 to 98% and containing as an active material from 10 to 20% by weight of cobalt based on the sum of nickel and cobalt; the alkaline storage battery using the same as a positive electrode and a mixed solution as an electrolyte comprising sodium hydroxide and potassium hydroxide. The battery has a high Ah efficiency in a wide temperature range, a higher energy density and a longer operating life in a low termperature of 0.degree. C. or less and a high temperature of 50.degree. C. or more, thereby providing a prismatic sealed alkaline storage battery for the power sources including cycle service use, such as electric vehicles.

Abstract: This invention is to provide a nickel-cadmium alkaline storage battery in which the content of nickel hydroxide and/or nickel oxide in a negative active material is from 2 to 60 wt% based on the total amount of cadmium, and the content of cadmium hydroxide in the negative active material is 0.95 or lower in terms of a weight ratio to nickel hydroxide in a positive active material; a manganese dioxide-cadmium alkaline storage battery in which the content of cadmium hydroxide in a negative active material in the discharged state is 0.84 or lower in terms of a weight ratio to manganese dioxide in a positive active material; and a silver oxide-cadmium alkaline storage battery in which the content of cadmium hydroxide in a negative active material in the discharged state is 1.36 or lower in terms of a weight ratio to silver in a positive active material.

Abstract: A sealed alkaline secondary battery with a cadmium negative electrode employs a micro-porous separator having circular or elliptic pores, to thereby eliminate the occurrence of internal short-circuiting and to improve the oxygen gas absorption ability of the battery.

Abstract: An alkaline storage battery is described including a positive electrode comprising as an active material a cobalt hydroxide base containing from about 15 to 65 wt % nickel hydroxide and a negative electrode comprising zinc or cadmium as an active material; the alkaline storage battery can be charged rapidly, has a high energy density, and the residual capacity of the battery can be easily measured by detection of the electromotive force of the battery.