Abstract: The present invention relates to a polar group-containing olefin copolymer (A?) which is produced through polymerization using a transition metal catalyst, which has a weight-average molecular weight falling within a specific range and which contains a polar group-containing monomer within a specific range; a multinary polar olefin copolymer (A?) indispensably containing a polar monomer component that has a norbornene skeleton and a carboxyl group or an acid anhydride group and having three or more types of monomer units; and a resin composition (C) containing a specific amount of a polar group-containing olefin copolymer (A) and a specific amount of an olefin resin (B).

Abstract: The present invention relates to a polar group-containing olefin copolymer (A?) which is produced through polymerization using a transition metal catalyst, which has a weight-average molecular weight falling within a specific range and which contains a polar group-containing monomer within a specific range; a multinary polar olefin copolymer (A?) indispensably containing a polar monomer component that has a norbornene skeleton and a carboxyl group or an acid anhydride group and having three or more types of monomer units; and a resin composition (C) containing a specific amount of a polar group-containing olefin copolymer (A) and a specific amount of an olefin resin (B).

Abstract: The present invention provides a metallocene complex capable of producing a homopolypropylene having a high melting point in the homopolymerization of propylene, and a production method of an olefin polymer using the same. The metallocene complex of the present invention is represented by formula [I].

Abstract: To provide an industrially useful ?-olefin•((meth)acrylic acid)-based olefin copolymer having both a high molecular weight and a high comonomer content, a catalyst component capable of realizing a production of two different kinds of ?-olefin•((meth)acrylic acid)-based olefin copolymers, and a production process using the catalyst. An ?-olefin•((meth)acrylic acid)-based olefin copolymer is produced by using a metal complex complexed with a ligand represented by the following formula (Y is phosphorus or arsenic) for a catalyst composition.

Abstract: The present invention provides a metallocene complex capable of producing a homopolypropylene having a high melting point in the homopolymerization of propylene, and a production method of an olefin polymer using the same. The metallocene complex of the present invention is represented by formula [I].

Abstract: To provide an industrially useful ?-olefin•((meth)acrylic acid)-based olefin copolymer having both a high molecular weight and a high comonomer content, a catalyst component capable of realizing a production of two different kinds of ?-olefin•((meth)acrylic acid)-based olefin copolymers, and a production process using the catalyst. An ?-olefin•((meth)acrylic acid)-based olefin copolymer is produced by using a metal complex complexed with a ligand represented by the following formula (Y is phosphorus or arsenic) for a catalyst composition.

Abstract: To provide an industrially useful ?-olefin.((meth)acrylic acid)-based olefin copolymer having both a high molecular weight and a high comonomer content, a catalyst component capable of realizing a production of two different kinds of ?-olefin.((meth)acrylic acid)-based olefin copolymers, and a production process using the catalyst. An ?-olefin.((meth)acrylic acid)-based olefin copolymer is produced by using a metal complex complexed with a ligand represented by the following formula (Y is phosphorus or arsenic) for a catalyst composition.

Abstract: The present invention relates to a polar group-containing olefin copolymer (A?) which is produced through polymerization using a transition metal catalyst, which has a weight-average molecular weight falling within a specific range and which contains a polar group-containing monomer within a specific range; a multinary polar olefin copolymer (A?) indispensably containing a polar monomer component that has a norbornene skeleton and a carboxyl group or an acid anhydride group and having three or more types of monomer units; and a resin composition (C) containing a specific amount of a polar group-containing olefin copolymer (A) and a specific amount of an olefin resin (B).

Abstract: A metallocene complex by which high uptake efficiency of ethylene and/or ?-olefin can be obtained compared with the conventional metallocene catalyst, and robber component having high molecular weight can be polymerized, and polymerization method of olefin. Metallocene complex (metallocene complex having furyl or thienyl group in which substituent exists at 5-position of indenyl ring, and substituent may exist at 2-position of indenyl ring, and the like) represented by the general formula [II], the catalyst for olefin polymerization characterized by comprising said metallocene complex, and polymerization method of olefin characterized that polymerization or copolymerization of olefin is carried out using said polymerization catalyst for olefin, and the like.

Abstract: A propylene-based polymer comprising the following component (A) insoluble in p-xylene at 25° C. and component (B) soluble in p-xylene at 25° C., wherein (i) the weight average molecular weight (Mw) measured with GPC is 100,000 to 1,000,000, (ii) the content of the component insoluble in hot p-xylene is 0.3% by weight or lower, and (iii) the degree of strain hardening (? max) in measurement of elongational viscosity is 2.0 or higher; and a method for producing the same, along with a resin composition comprising a propylene-ethylene copolymer (Z) in an amount of 50.0 to 99.9% by weight and a propylene-based polymer (M) in an amount of 0.1 to 50.0% by weight. Component (A): a component (CXIS) insoluble in p-xylene at 25° C., having requirements specified by (A1) to (A5). Component (B): a component (CXS) is soluble in p-xylene at 25° C., having requirements specified by (B1) to (B4).

Abstract: A propylene-based polymer which is suitably applicable to foam molding, sheet molding, blow molding or the like, because of having good flow characteristics, high melt tension, high swell ratio and thus good molding workability. It is attained by a propylene-based polymer or the like characterized by satisfying the following requirements (i) to (vi). Requirement (i): MFR is 0.1 g/10 minutes to 100 g/10 minutes. Requirement (ii): Q value by GPC is 3.5 to 10.5. Requirement (iii): ratio of components with a molecular weight of equal to or higher than 2,000,000, in a molecular weight distribution curve obtained by GPC, is equal to or larger than 0.4% by weight and less than 10% by weight. Requirement (iv): components, which elute at a temperature of equal to or lower than 40° C., are equal to or less than 3.0% by weight, in temperature rising elution fractionation by ODCB. Requirement (v): isotactic triad fraction (mm) measured with 13C-NMR is equal to or higher than 95%.

Abstract: To provide an industrially useful ?-olefin.((meth)acrylic acid)-based olefin copolymer having both a high molecular weight and a high comonomer content, a catalyst component capable of realizing a production of two different kinds of ?-olefin.((meth)acrylic acid)-based olefin copolymers, and a production process using the catalyst. An ?-olefin.((meth)acrylic acid)-based olefin copolymer is produced by using a metal complex complexed with a ligand represented by the following formula (Y is phosphorus or arsenic) for a catalyst composition.

Abstract: A metallocene complex by which high uptake efficiency of ethylene and/or ?-olefin can be obtained compared with the conventional metallocene catalyst, and rubber component having high molecular weight can be polymerized, and polymerization method of olefin. Metallocene complex (metallocene complex having furyl or thienyl group in which substituent exists at 5-position of indenyl ring, and substituent may exist at 2-position of indenyl ring, and the like) represented by the general formula [I], the catalyst for olefin polymerization characterized by comprising said metallocene complex, and polymerization method of olefin characterized in that polymerization or copolymerization of olefin is carried out using said polymerization catalyst for olefin, and the like.

Abstract: A propylene resin composition which is a three-component material is improved in rigidity, heat resistance, and impact resistance while maintaining a satisfactory balance among these and further improved in low-temperature (about ?30° C.) impact resistance. A propylene resin composition as described in the specification.

Abstract: A propylene-based polymer which is suitably applicable to foam molding, sheet molding, blow molding or the like, because of having good flow characteristics, high melt tension, high swell ratio and thus good molding workability. It is attained by a propylene-based polymer or the like characterized by satisfying the following requirements (i) to (vi). Requirement (i): MFR is 0.1 g/10 minutes to 100 g/10 minutes. Requirement (ii): Q value by GPC is 3.5 to 10.5. Requirement (iii): ratio of components with a molecular weight of equal to or higher than 2,000,000, in a molecular weight distribution curve obtained by GPC, is equal to or larger than 0.4% by weight and less than 10% by weight. Requirement (iv): components, which elute at a temperature of equal to or lower than 40° C., are equal to or less than 3.0% by weight, in temperature rising elution fractionation by ODCB. Requirement (v): isotactic triad fraction (mm) measured with 13C-NMR is equal to or higher than 95%.

Abstract: A propylene-based polymer comprising the following component (A) insoluble in p-xylene at 25° C. and component (B) soluble in p-xylene at 25° C., wherein (i) the weight average molecular weight (Mw) measured with GPC is 100,000 to 1,000,000, (ii) the content of the component insoluble in hot p-xylene is 0.3% by weight or lower, and (iii) the degree of strain hardening (? max) in measurement of elongational viscosity is 2.0 or higher; and a method for producing the same, along with a resin composition comprising a propylene-ethylene copolymer (Z) in an amount of 50.0 to 99.9% by weight and a propylene-based polymer (M) in an amount of 0.1 to 50.0% by weight. Component (A): a component (CXIS) insoluble in p-xylene at 25° C., having requirements specified by (A1) to (A5). Component (B): a component (CXS) is soluble in p-xylene at 25° C., having requirements specified by (B1) to (B4).

Abstract: A propylene resin composition which is a three-component material is improved in rigidity, heat resistance, and impact resistance while maintaining a satisfactory balance among these and further improved in low-temperature (about ?30° C.) impact resistance. A propylene resin composition comprising: 60-95 wt % of a crystalline propylene polymer ingredient (a) comprising a propylene homopolymer ingredient or a copolymer of propylene and up to 3 wt % ethylene or an ?-olefin having 4-20 carbon atoms; and 40-5 wt % of a propylene/ethylene copolymer ingredient (b), wherein the ingredients are polymerized using a metallocene catalyst, and the composition satisfies the following properties i) to iv): i) A melting point obtained by differential scanning calorimetry (DSC) is 156° C. or higher, ii) A proportion of the copolymer ingredient (b) determined by a temperature rising elution fractionation (TREF) fractionating at three levels of temperature of 40° C., 100° C., and 140° C.

Abstract: A catalyst component for olefin polymerization, which comprises an ion-exchange layered silicate having the following features 1 and 2: feature 1: in a pore size distribution curve calculated from desorption isotherm by nitrogen adsorption-desorption method, a pore diameter Dm showing a maximum peak intensity DVM is from 60 to 200 Å; and feature 2: in a pore size distribution curve calculated from desorption isotherm by nitrogen adsorption-desorption method, a pore diameter Dm1/2 (Å) on the smaller pore size side corresponding to a ½ peak intensity of the maximum peak intensity DVM has a relation of Dm1/2/Dm of at least 0.65 and less than 1, provided that the largest value is employed when there are a plurality of Dm1/2 values.

Abstract: An olefin polymerization catalyst comprising the following components (A) and (B): Component (A): an ion-exchange layered silicate having an acid site of at most −8.2 pKa, the amount of the acid site is equivalent to at least 0.05 mmol/g of 2,6-dimethylpyridine consumed for neutralization; and Component (B): a compound of a transition metal belonging to Group 3 to Group 12 of the Periodic Table.

Abstract: A catalyst component for olefin polymerization, which comprises an ion-exchange layered silicate having the following features 1 and 2: