Abstract: The present application relates to a method to prevent the emission of hydrogen sulphide in the production of hot bitumen or asphalt having a temperature of between 150 and 200° C., wherein the method comprises the steps of providing a bituminous or asphalt mixture, heating the mixture until a temperature of between 150-200° C. and adding an aqueous calcium nitrate solution or a calcium nitrate powder while mixing the bituminous or asphalt mixture. The present application furthermore relates to the use of an aqueous calcium nitrate solution or a calcium nitrate powder during mixing of a bituminous or asphalt mixture in the production of a hot bitumen or asphalt having a temperature of between 150 and 200° C. to prevent the emission of hydrogen sulphide.

Abstract: The present application relates to a method to prevent the emission of hydrogen sulphide in the production of hot bitumen or asphalt having a temperature of between 150 and 200° C., wherein the method comprises the steps of providing a bituminous or asphalt mixture, heating the mixture until a temperature of between 150-200° C. and adding an aqueous calcium nitrate solution or a calcium nitrate powder while mixing the bituminous or asphalt mixture. The present application furthermore relates to the use of an aqueous calcium nitrate solution or a calcium nitrate powder during mixing of a bituminous or asphalt mixture in the production of a hot bitumen or asphalt having a temperature of between 150 and 200° C. to prevent the emission of hydrogen sulphide.

Abstract: The invention relates to a setting accelerator for a dry mortar blend, the setting accelerator being in the form of a powder comprising calcium nitrate and having a water content between 0.1% and 20%. The invention furthermore relates to a process for producing such a setting accelerator, wherein either prills and/or granules comprising calcium nitrate and a different nitrate salt are processed forming a powder comprising calcium nitrate and the different nitrate salt and having a water content of higher than 5% and lower than 20%, either an aqueous solution at least comprising dissolved calcium nitrate is spray dried at a temperature between 150° C. and 250° C., forming a powder comprising at least calcium nitrate and having a water content between 0.1% and 20%, the powder serving as the setting accelerator.