Abstract: The invention relates to a process for devulcanizing a vulcanized rubber mixture, comprising the following steps: A) providing or producing a vulcanized rubber mixture, B) comminuting the vulcanized rubber mixture into a granulate of vulcanized rubber particles, C) extruding the vulcanized rubber particles produced in step B) in a twin-screw extruder to form a devulcanized rubber mixture, wherein, during the extruding in step C) at least one regeneration reagent is added to the extruded rubber particles, wherein the regeneration reagent comprises at least one silane, at least one plasticizer, at least one aging stabilizer or mixtures thereof. The invention also comprises an apparatus for performing the method and the uses of the apparatus, and a rubber mixture and also a pneumatic vehicle tyre or a technical rubber article comprising a component composed of the rubber mixture.

Abstract: The invention relates to a process for devulcanizing a vulcanized rubber mixture, comprising the following steps: A) providing or producing a vulcanized rubber mixture, B) comminuting the vulcanized rubber mixture to a granular material composed of vulcanized rubber particles, where the vulcanized rubber particles have a maximum particle diameter of 100 mm, C) extruding the vulcanized rubber particles produced in step B) in a twin-screw extruder at a shear rate of less than 100 s?1, where the temperature of the vulcanized rubber particles during extrusion is less than 200° C., to give a devulcanized rubber mixture having a temperature above 100° C., D) cooling the devulcanized rubber mixture in a further kneading unit, so as to give a devulcanized rubber mixture having a temperature in the range from 50° C. to 100° C. The invention further relates to an apparatus for performing the process and to the use of the apparatus for devulcanization of a vulcanized rubber mixture.

Abstract: The invention relates to a process for devulcanizing a vulcanized rubber mixture, comprising the following steps: A) providing or producing a vulcanized rubber mixture, B) comminuting the vulcanized rubber mixture into a granulate of vulcanized rubber particles, C) extruding the vulcanized rubber particles produced in step B) in a twin-screw extruder to form a devulcanized rubber mixture, wherein, during the extruding in step C) at least one regeneration reagent is added to the extruded rubber particles, wherein the regeneration reagent comprises at least one silane, at least one plasticizer, at least one aging stabilizer or mixtures thereof. The invention also comprises an apparatus for performing the method and the uses of the apparatus, and a rubber mixture and also a pneumatic vehicle tyre or a technical rubber article comprising a component composed of the rubber mixture.

Abstract: The invention relates to a process for devulcanizing a vulcanized rubber mixture, comprising the following steps: A) providing or producing a vulcanized rubber mixture, B) comminuting the vulcanized rubber mixture to a granular material composed of vulcanized rubber particles, where the vulcanized rubber particles have a maximum particle diameter of 100 mm, C) extruding the vulcanized rubber particles produced in step B) in a twin-screw extruder at a shear rate of less than 100 s?1, where the temperature of the vulcanized rubber particles during extrusion is less than 200° C., to give a devulcanized rubber mixture having a temperature above 100° C., D) cooling the devulcanized rubber mixture in a further kneading unit, so as to give a devulcanized rubber mixture having a temperature in the range from 50° C. to 100° C. The invention further relates to an apparatus for performing the process and to the use of the apparatus for devulcanization of a vulcanized rubber mixture.