Abstract: The invention provides a thermoplastic resin composition, which does not substantially compromise color rendering and flame retardance of a thermoplastic resin and has high impact resistance, slidability, and chemical resistance in a wide scope of environmental conditions ranging from low temperature to high temperature. A graft copolymer (GF2) containing rubber is a graft copolymer containing rubber formed by performing graft polymerization of 1 or more vinyl monomers on a composite rubber containing a polyorganosiloxane (B1) and a polyalkyl (meth)acrylate (B2). The content of a component derived from a silane compound containing a vinyl-based polymerizable group in the polyorganosiloxane (B1) is 1 mass % to 10 mass %. The volume-average particle size of the graft copolymer containing rubber is 300 nm to 2000 nm. The content of the polyorganosiloxane (B1) in the graft copolymer containing rubber is 70 mass % to 98 mass %. An acetone soluble matter is 5.0 mass % or more and 30.0 mass % or less.

Abstract: The invention provides a thermoplastic resin composition, which does not substantially compromise color rendering and flame retardance of a thermoplastic resin and has high impact resistance, slidability, and chemical resistance in a wide scope of environmental conditions ranging from low temperature to high temperature. A graft copolymer (GF2) containing rubber is a graft copolymer containing rubber formed by performing graft polymerization of 1 or more vinyl monomers on a composite rubber containing a polyorganosiloxane (B1) and a polyalkyl (meth)acrylate (B2). The content of a component derived from a silane compound containing a vinyl-based polymerizable group in the polyorganosiloxane (B1) is 1 mass % to 10 mass %. The volume-average particle size of the graft copolymer containing rubber is 300 nm to 2000 nm. The content of the polyorganosiloxane (B1) in the graft copolymer containing rubber is 70 mass % to 98 mass %. An acetone soluble matter is 5.0 mass % or more and 30.0 mass % or less.

Abstract: Disclosed are a method of producing a graft copolymer, comprising polymerizing a vinyl monomer (B) containing a polyfunctional vinyl monomer (b1) in the presence of a polyorganosiloxane rubber (A) comprising more than 20% by mass of a toluene-insoluble matter, wherein a mass percentage of the polyfunctional vinyl monomer (b1) is 11 to 19% by mass based on 100% by mass of a total amount of the polyorganosiloxane rubber (A) and the vinyl monomer (B); a graft copolymer obtained by the method; a resin composition being prepared by blending the graft copolymer with a resin and having high impact resistance and heat resistance and sufficient flame retardancy; and a molded article obtained by molding the resin composition.

Abstract: [Object] Provided is a reinforcing agent for resin that is able to impart excellent impact resistance, resistance to thermal coloration, and resistance to moist heat to a polycarbonate resin. [Solving Means] Disclosed is a reinforcing agent for polycarbonate resin which includes a rubber-like graft polymer, in which a quantity of the ?YI value that is increased by a heat treatment at a temperature of 140° C. for 12 hours and measured for a molded article obtained by molding 3 parts by mass of the reinforcing agent for polycarbonate resin and 97 parts by mass of an aromatic polycarbonate resin having a viscosity average molecular weight of 24,000 under a specific condition is 36 or less and a quantity of the ?MFR value increased by a heat treatment for 60 hours under a condition of a temperature of 120° C. and a relative humidity of 100% is 3 or less. Disclosed is also a resin composition including the reinforcing agent for polycarbonate resin.

Abstract: Disclosed are a method of producing a graft copolymer, comprising polymerizing a vinyl monomer (B) containing a polyfunctional vinyl monomer (b1) in the presence of a polyorganosiloxane rubber (A) comprising more than 20% by mass of a toluene-insoluble matter, wherein a mass percentage of the polyfunctional vinyl monomer (b1) is 11 to 19% by mass based on 100% by mass of a total amount of the polyorganosiloxane rubber (A) and the vinyl monomer (B); a graft copolymer obtained by the method; a resin composition being prepared by blending the graft copolymer with a resin and having high impact resistance and heat resistance and sufficient flame retardancy; and a molded article obtained by molding the resin composition.