Abstract: Disclosed is a method with which it is possible to observe a biological sample in a living state, without significant restrictions due to the properties of the sample or due to a structural body accommodating the sample. To observe a target sample on a sample stage using a SEM including a radiation source for electron beam irradiation, the method includes: a step of bringing an insulating and electron-permeable thin film into contact with the target sample in such a way as to follow a surface on the radiation source side of the target sample, and sealing the target sample in a gap between the film and the sample stage; and a step of radiating an electron beam onto the target sample from the radiation source through the film.

Abstract: The present invention provides a bearing material that is excellent in durability and is capable of maintaining wear resistance over a long period of time. The bearing material of the present invention is a high wear-resistance bearing material 10 for being used under a humid environment comprising: a base body 12 made of a polymer material having a methylene group; and a polymer layer 30 covering a bearing surface 16 of the substrate 12, the polymer layer 30 comprising polymer chains which have a phosphorylcholine group and are grafted from the bearing surface 16, wherein a phosphoric index of the sliding surface 16 which is calculated by dividing a peak intensity of phosphate group in an infrared spectrum measured on the sliding surface by a peak intensity of the methylene group therein is not less than 0.28.

Abstract: The present invention provides a bearing material that is excellent in durability and is capable of maintaining wear resistance over a long period of time. The bearing material of the present invention is a high wear-resistance bearing material 10 for being used under a humid environment comprising: a base body 12 made of a polymer material having a methylene group; and a polymer layer 30 covering a bearing surface 16 of the substrate 12, the polymer layer 30 comprising polymer chains which have a phosphorylcholine group and are grafted from the bearing surface 16, wherein a phosphoric index of the sliding surface 16 which is calculated by dividing a peak intensity of phosphate group in an infrared spectrum measured on the sliding surface by a peak intensity of the methylene group therein is not less than 0.28.